In this present research work, corrosion behaviour of grit blasted AISI 410 steel substrate coated with NiCr/Al2O3,NiCr/ZrO2 particles was investigated using salt spray test as per ASTM B117. Coatings were prepared using air Plasma spray process. Nickel chromium was used as bond coat for obtaining good fastening between the base metal and coated particles. The microstructures of the coated and un-coated specimens were characterized using scanning electron microscope and optical microscope. Distribution coated particle was found uniform throughout the steel substrate was revealed from SEM microphotographs. The obtained results shows significant improvement in corrosion resistance and micro hardness for NiCr/Al2O3 and NiCr/ZrO2 coating deposited on steel by plasma spray process than the as sprayed base steel substrates.
Combined slurry and cavitation erosion resistance of surface modified SS410 stainless steel H J Amarendra, M S Pratap, S Karthik et al. Abstract. Slurry erosion is an implicit problem in many engineering industrial components such as ore carrying pipelines, slurry pumps and extruders. Even the water turbine blades are subjected to erosive wear when the water contains considerable amount of silt. In the present study, Al 2 O 3 -40%TiO 2 powder particles of average particle size of 50 micrometer were deposited on EN56B martenistic stainless steel by atmospheric plasma spray technique. Ni/Cr was pre coated to work as bond coat for good adhesion between coating and the substrate material. A coating thickness of 200 micrometer was achieved. Coated and un-coated substrates were subjected to slurry erosion test as per ASTM G-119 standard. Slurry erosion test rig was used to evaluate the erosion properties at room temperature condition by varying the spindle speed. Scanning electron microphotographs were taken before and after the slurry erosion test. Microstructures reveal uniform distribution of coating materials. Eroded surface shows lip, groove, and crater formation and dense coating resulting in less porosity. Micro hardness test was evaluated and reported. EDX analysis confirms the presence of Al, Ti and O 2 particles. It was observed that, Al 2 O 3 -40%TiO 2 coated substrates exhibit superior erosion resistance as compared to un-coated substrates due to higher hardness and less coating porosity.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.