Background:There is necessary of dry operating field for bonding of orthodontic brackets. The presence of moisture can alter the bond strength. Hence, the aim of the present study was to evaluate the shear bond strength of orthodontic brackets with different adhesives.Materials and Methods:In this in vitro study, a total of 100 orthodontically extracted premolars with sound crown structure were divided into 4 equal groups of different primers. Bonding on the buccal surface of all teeth was done after acid etching with upper premolar brackets using different primers followed by light curing. Shear bond strength was evaluated with or without salivary contamination with both adhesives. A shear force for deboning the bracket was done with universal testing machine. The debonded specimens were examined at ×10 magnification to check site of bond failure and remaining adhesive on tooth using adhesive remnant index (ARI). The obtained data were statistically evaluated using SPSS 20 for Windows (SPSS Inc., Chicago, IL, USA) using ANOVA, Kolmogorov–Smirnov, and Levene's test at the statistical significance of P < 0.05.Results:Transbond Plus showed higher shear bond strength of 8.92 MPa under dry and 5.65 MPa with saliva contamination over Transbond XT of 7.24 MPa under dry and 2.43 MPa with saliva contamination, respectively. Higher ARI score was found without contamination in both adhesives.Conclusion:Transbond Plus hydrophilic resin had good shear bond strength under both dry and contamination condition compared to hydrophobic Transbond XT resin material.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.