The stabilizing role of carboxymethyl groups on the conformal deposition of Ag NPs over cellulosic fibers was elucidated while developing a method for the deposition of silver nanoparticles (NPs) on cellulose acetate (CA), cellulose and partially carboxymethylated cellulose (CMC) electrospun fibers. CMC fibers were prepared through judicious anionization of deacetylated cellulose acetate fibers. Ag NPs were chemically reduced from silver nitrate using sodium borohydride and further stabilized using citrate. Ag NPs were directly deposited onto CA, cellulose and CMC electrospun fibers at pH conditions ranging from 2.5 to 9.0. The resulting composites of Ag/fiber were characterized by field emission scanning electron microscopy (FESEM) and energydispersive X-ray spectroscopy (EDX). The results revealed that the amount of Ag agglomerates and NPs deposited on CMC fibers was higher than that deposited on cellulose fibers at similar pH conditions, and that barely any Ag agglomerates or NPs were deposited on the CA fibers. These results implied that functional groups on the cellulose backbone played two important roles in the deposition of NPs as follows: (1) Hydrogen bonding was the main driving force for agglomeration of NPs when the medium pH was below 4.4, which corresponds to the pKa of carboxylic acid groups; (2) Carboxymethyl groups could replace citrate groups as stabilizers allowing the fabrication of a uniform and evenly distributed Ag NPs layer over CMC fibers at higher pH values. This report also highlights the importance of the substrate's surface charge and that of the pH of the medium used, on the deposition of NPs. The composite of Ag NPs on CMC electrospun fibers appears to be a promising candidate for wound dressing applications due to its superior antibacterial properties originated by the uniform and even distribution of Ag NPs on the surface of the fibers and the wound healing aptness of the CMC fibers.
Hydrogels
as a wound dressing, integrated with ultrastretchability,
rapid self-healing, and excellent antimicrobial activity, are in high
demand, particularly for joint skin wound healing. Herein, a multifunctional
and ductile composite hydrogel was developed using poly(vinyl alcohol)
(PVA)-borax gel as a matrix that was synergized or dual-reinforced
with dopamine-grafted oxidized carboxymethyl cellulose (OCMC-DA) and
cellulose nanofibers (CNF). Moreover, neomycin (NEO), an aminoglycoside
antibiotic with multifunctional groups, was incorporated into the
hydrogel network as both an antibacterial agent and a cross-linker.
The dynamic reversible borate ester linkages and hydrogen bonds between
OCMC-DA, PVA, and CNF, along with dynamic cross-linking imine linkages
between NEO and OCMC-DA, endowed the hydrogel with excellent self-healing
ability and stretchability (3300%). The as-reinforced networks enhanced
the mechanical properties of hydrogels significantly. More remarkably,
the composite hydrogel with improved biodegradability and biocompatibility
is pH-responsive and effective against a broad spectrum of bacteria,
which is attributed to the controllable release of NEO for steady
availability of the antibiotic on the wound location. Overall, the
antimicrobial hydrogel with rapid self-healing and reliable mechanical
properties holds significant promise as dressing material for wound
healing.
The association of a symmetric polyoxyethylene-polyoxypropylene-polyoxyethylene (PEO(19)-PPO(29)-PEO(19)) triblock copolymer adsorbed from aqueous solutions onto polypropylene (PP), polyethylene (PE), and cellulose surfaces was probed using Atomic Force Microscopy (AFM). Significant morphological differences between the polyolefin substrates (PP and PE) and the cellulose surfaces were observed after immersion of the films in the PEO(19)-PPO(29)-PEO(19) solutions. When the samples were scanned, while immersed in solutions of the triblock copolymer, it was revealed that the structures adsorbed on the polyolefin surfaces were smoothed by the adsorbed PEO(19)-PPO(29)-PEO(19). In contrast, those structures on the hydrophilic cellulose surfaces were sharpened. These observations were related to the roughness of the substrate and the energy of interaction between the surfaces and the PEO and PPO polymer segments. The interaction energy between each of the blocks and the surface was calculated using molecular dynamics simulations. It is speculated that the associative structures amply reported in aqueous solution at concentrations above the critical micelle concentration, CMC, are not necessarily preserved upon adsorption; instead, it appears that molecular arrangements of the anchor-buoy type and hemimicelles prevail. The reported data suggests that the roughness of the surface, as well as its degree of hydrophobicity, have a large influence on the nature of the resulting adsorbed layer. The reported observations are valuable in explaining the behavior of finishing additives and lubricants commonly used in textile and fiber processing, as well as the effect of the morphology of the boundary layers on friction and wear, especially in the case of symmetric triblock copolymers, which are commonly used as antifriction, antiwear additives.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.