Ultrasonic nanocrystal surface modification (UNSM) technology is a novel surface modification technology that can improve the mechanical and tribological properties of interacting surfaces in relative motion. UNSM treatment was utilized to improve the wear resistance fatigue strength of slim bearing rings made of SAE52100 bearing steel without damaging the raceway surfaces. In this study, wear and fatigue results that were subjected to different impact loads of the UNSM treatment were investigated and compared with those of the untreated specimen. The microhardness of the UNSM-treated specimens increased by about 20%, higher than that of the untreated specimens. The X-ray diffraction analysis showed that a compressive residual stress of more than 1,000 MPa was induced after the UNSM treatment. Also, electron backscatter diffraction analysis was used to study the surface structure and nanograin refinement. The results showed that the rolling contact fatigue life and the rotary bending fatigue strength of the UNSM-treated specimens increased by about 80% and 31%, respectively, compared to those of the untreated specimen. These results might be attributed to the increased microhardness, the induced compressive residual stress, and the nanocrystal structure modification after the UNSM treatment. In addition, the fracture surface analysis showed that the fish eye crack initiation phenomenon was observed after the UNSM treatment.
Owing to the superior properties of stainless steel it is pertinent to make use of it in various applications of automotive, aerospace, nuclear, chemical and cryogenic products. This paper describes a study of friction characteristics of SUS304 and SUS630 stainless steel disk specimens against silicon nitride Si3N4 ball in dry, grease-, and oil-lubricated conditions and wear characteristics in dry condition in sliding contact. The ultrasonic nanocrystal surface modification (UNSM) technology was applied to those disk specimens and its friction and wear properties were compared with polished one. The experiment was conducted with a pin-on-disk tribo tester using ball-on-disk contact geometry at room temperature. The experiment results show that in dry, greased- and oil-lubrication conditions the coefficient of friction of UNSM-treated specimens was lower and constant than polished specimens and in dry condition the wear rate was also smaller than polished one. Micro dimples made by UNSM treatment contribute those effects.
In this study, two different AISI 52100 bearing and D2 tool steels were subjected to ultrasonic nanocrystalline surface modification (UNSM) technique at ambient and high temperature of 500 °C. The objective of this study is to characterize the microstructure and to investigate the effectiveness of UNSM technique on the friction and wear behavior of those steels. The friction and wear behavior of the specimens against AISI52100 bearing steel ball with a diameter of 10 mm was carried out using a micro-tribo tester under dry conditions. The hardness with respect to depth from the top surface was measured using a microhardness. The change in the microstructure of the specimens before and after UNSM treatment was characterized by scanning electron microscopy (SEM). The findings from this preliminary study are expected to be implemented to the bearings and tools to increase the efficiency and performance of the components.
Rolling contact fatigue (RCF) is known as the dominant factor determining the service life of bearing materials. In this work, the fatigue life of the typical bearing alloy was significantly improved by introducing a nanoskin layer on the surfaces of the test specimens. The nanoskin layer structure was obtained by means of the ultrasonic nanocrystal surface modification (UNSM) technology. The microstructure of the nanoskin was analyzed via scanning electron microscope (SEM), electron back-scatter diffraction (EBSD), and transmission electron microscope (TEM). SUJ2 and SUJ3 bearings at different states of fatigue were subjected to UNSM treatment. For SUJ2 a rotary-bending fatigue (RBF) life average for three untreated specimens was chosen as 100% life, and then several untreated specimens were fatigued to 25%, 50% and 75% of life with subsequent UNSM treatment. This way used bearing conditions were simulated. The rotary-bending fatigue (RBF) tests of fatigue+UNSM SUJ2 specimens have shown 377-430% improvement of fatigue life, comparing to untreated specimens. For SUJ3 a RCF life untreated specimen was chosen as 100% life, and then several specimens were fatigued to approximately 100% of surface damage with subsequent UNSM treatment. Thus damaged surface conditions were simulated. The RCF tests of fatigue+UNSM SUJ3 specimens have shown 218% improvement of fatigue life, comparing to untreated specimens. This indicates the possibility of the restoration of the RCF life of bearing alloys by means of nanoskin treatment via UNSM technology.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.