The mechanical properties of polyamide 6 glass fiber (PA6/GF) long-fiber-reinforced thermoplastic (LFT) composites were characterized by studying the process conditions in terms of manufacturing methods (direct extrusion and pultrusion) and material characteristics (void content and fiber volume fraction). The LFT composites prepared through the pultrusion process have higher mechanical properties than those prepared via the direct extrusion process. The PA6/GF composite prepared via pultrusion had the tensile and flexural strengths of 233 MPa and 338 MPa, respectively. The impact strength measured using the Izod method was 296 J/m, which is 64% higher than that of the composite fabricated via the direct process. The optical microscope images showed that the glass fiber length of the pultruded composites is longer than the fiber length of the direct composites, leading to higher mechanical properties of the LFT composites prepared through the pultrusion process. Moreover, the interfacial shear strength between the resin and the fiber, measured via single fiber pullout tests, can account for the higher fiber reinforcing efficiency. If the void content of a composite is sufficiently small to not be detrimental to the composites, the mechanical properties are observed to be proportional to the fiber volume fraction of the composites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.