Highly porous cordierite ceramic by using of talcum, kaolinite and γ-alumina was obtained by method of slip casting of concentrated suspension. Additives of amorphous silica and non-stabilized zirconia in the amount of 5 wt% were used. Sintering temperature of dried samples was in range of 1250 – 1450°C. All the samples contain crystalline phases of cordierite, mullite and corundum but, depending on the additives, as a result of sintering in addition forms spinel, cristobalite or zircon (ZrSiO4). Porosity of obtained materials changes in large scale from 42 to 59 per cent; it is influenced by both sintering temperature and composition. Compressive strength increases with the addition of zirconia. In comparison, compressive strength of samples without additives or with silica additive does not exceed 3.5 MPa. The increase of coefficient of thermal expansion depends both on the composition and sintering temperature. ZrO2 additive increases the coefficient of thermal expansion considerably.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.