Garnet-type structured electrolytes are considered a key technology for the next generation of lithium-ion batteries such as all-solid-state batteries. Cubic Garnet-type solid oxides with composition Li5+xLa3(Nb2−xZrx)O12 (x between 0 and 1.5) were synthesized by solid-state reaction and sintered by spark plasma sintering. Powder characterization indicates the formation of solid solution with high chemical homogeneity and spherical particles. High relative densities (>96%) were obtained by spark plasma sintering at 950 °C for 10 min and pressure application of 50 MPa. Although the formation of secondary phase La2Zr2O7 was identified by the X-ray diffraction patterns of Zr-doped pellets, it has been eliminated for x = 0.75 and 1 by conventional heat treatment at 850 °C for 1 h. High ionic conductivity values were attained for x ≥ 0.75, reaching a maximum value in the order of 10−4 S.cm−1 at 25 °C with activation energy of 0.38 eV. The results indicated that Zr4+ promoted significant increasing of the lithium-ion conductivity by lowering the activation energy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.