No abstract

Given the lower mechanical properties of most bulk-fill materials compared to a highly filled nano-hybrid composite, their use for restorations under high occlusal load is subject to caution. Further, the swelling behaviour of some of the bulk-fill materials may be a reason for concern, which highlights the critical requirement for a veneering material, not only to improve aesthetic quality of the translucent material, but to reduce the impact of degradation.

Mechanical properties and filler characteristics significantly vary among modern RBCs and the current classification does not accurately illustrate either. Further, the chemical stability of RBCs differed, highlighting differences in resin and silane composition. Since E and sorption were well correlated to the filler content, a simple and unambiguous classification based on such characteristic is suggested, with three levels (ultra-low fill, low-fill and compact resin composites).

No abstract

Three types of low-shrinkage composites are today commercially available: Ormocers, cationic ring-opening curing systems and highly filled methacrylate-based materials, which cure via free-radical polymerization mechanisms. The aim of this study was to characterize the inorganic fraction of materials belonging to each type and to compare their mechanical properties. Two Ormocers (Admira and an experimental Ormocer V35694), one ring-opening composite (Filtek Silorane) and five methacrylate-based composites [Filtek Supreme XT, Tetric EvoCeram, Grandio, Synergy D6 (Coltène-Whaledent, Langenau, Germany) and an experimental material, V34930] were tested. Inorganic fillers were quantified by thermogravimetric analysis and morphologically characterized by scanning electron microscopy. Dynamic modulus was determined by an impulse excitation technique, static elastic moduli and flexural strength by a three-point bending method. The results were analyzed using ANOVA tests (P < 0.05) and linear correlations. Grandio, V34930 and V35694 exhibited significantly higher filler mass fractions. Both dynamic and static moduli of Grandio and V34930 were significantly higher than the other materials (P < 0.05), although no significant difference in flexural strength was observed between material type (P > 0.05). From the present findings, it was suggested that V35694 and Filtek Silorane exhibit comparable properties to conventional methacrylate-based composites, although clinically the cavity type and location must guide material choice. Under high occlusal load, the use of Grandio and V34930 might be favoured. For small cavities, alternative technologies could be preferred as the need for mechanical resistance is lower and the potential for stress generation is greater.

No abstract

SUMMARY This paper assesses the effects of light characteristics and irradiation time on the Vickers microhardness (VH) of a dual-photoinitiator commercial composite and on temperature increase in the pulp chamber (∆T). Four recent light-emitting diodes (LEDs)-bluephaseG2 (BG2), bluephase16i (B16i), G-Light (G) andFreelight2 (F2)-and one control halogen light (XL3000-X) were tested on two shades of Tetric EvoCeram (A2 and Bleach XL), whose respective commercial formulations differed based on their concentration of camphorquinone and lucirin TPO. Three different irradiation times were applied-10, 20 and 40 seconds-and VH was measured on the upper and lower surfaces of 2-mm thick samples. The ∆T was measured by using a K-type thermocouple inserted into the pulp chamber of a molar that had been prepared to obtain a 2-mm thickness of dentin. The measurements were made either during polymerization of a 2 mm composite (Shade A2 Clinical RelevanceThis paper provides practitioners with useful information on the importance of aligning the spectra of the LCU and the material in terms of polymerization efficiency and temperature rise in the pulp chamber. The ∆T values obtained with uncovered tooth were generally higher than those obtained with a 2-mm layer of composite. In conclusion, this research emphasizes that a perfect correspondence between light and material spectra is of prime concern, both to insure optimal polymerization and to limit heating in the pulp chamber. Some reduction in curing time is possible, but only within certain limits.

No abstract