No abstract

Scarcity of raw materials, reduction of greenhouse gas emissions and reduction of waste disposal in landfills are leading to the development of more sustainable building materials. Based on these lines, this work studies the incorporation of biomass bottom ashes into ceramic materials for brick manufacture, in order to reuse this currently unused waste and reduce clay extraction operations. To this end, different groups of samples were made with different combinations of clay and biomass bottom ashes, from 100% clay to 100% biomass bottom ashes. These samples were shaped, sintered and subjected to the usual physical tests in ceramics. In turn, the mechanical resistance, color and leaching of the contaminating elements present were studied. The physical and mechanical tests showed that the results of all the families were adequate, achieving compressive strengths of over 20 MPa and leaching of the contaminating elements acceptable by the regulations. Therefore, a sustainable range of ceramics was developed, with specific properties (porosity, density, resistance and color), with a waste that is currently unused and sustainable with the environment.

Mining activity is essential for the social welfare of the population. However, this activity produces a series of mining waste. These mining wastes, if not properly treated, can produce significant environmental pollution. This study develops the incorporation of tailings from washing plants in ceramic materials for bricks in order to retain the contaminating elements in the ceramic matrix. To this end, firstly, a physical and chemical characterisation of the mining waste is carried out and different groups of samples are conformed with clay and mining waste. These conformed samples with mining waste are evaluated through different physical and mechanical tests typical in the ceramic industry, studying the variation of properties by the incorporation of the waste. In turn, the leachates from the groups of conformed samples are analyzed, confirming the retention of the contaminating elements of the mining waste in the ceramic matrix. The results of these tests showed that ceramics can be made for bricks with up to 90% mining waste, obtaining physical and mechanical properties acceptable regarding the regulations and retaining the contaminating elements in the ceramic matrix, as confirmed by the leachate tests.

The construction sector is one of the most demanding of raw materials that exist at present. In turn, the greenhouse gas emissions that it produces are important. Therefore, at present there are several lines of research in which industrial by-products are incorporated for the manufacture of bituminous mixtures and the reduction of CO2 emissions, framed inside the circular economy. On the base of the aforementioned, in this research, bituminous mixtures of the Stone Mastic Asphalt type were developed with electric arc furnace slag, ladle furnace slag and discarded cellulose fibers from the papermaking industry. To this end, the waste is first characterized physically and chemically, and its properties evaluated for use in bituminous mixtures. Later, different groups of samples are conformed with conventional materials and with the waste in order to be able to compare the physical and mechanical properties of the obtained bituminous mixtures. The physical tests carried out were bulk density, maximum density and void index, as well as the Marshall test for the evaluation of the strength and plastic deformations of all the bituminous mixtures manufactured. The study and evaluation of the results showed that the incorporation of slag makes it possible to absorb a greater percentage of bitumen and obtain better mechanical properties, while maintaining a similar deformation and void content. Therefore, it is feasible to use the mentioned slags to create sustainable, resistant and suitable pavements for important traffic.

The road construction sector is one of the most raw material-intensive sectors in existence. As a result, it has a significant impact on the environment. For this reason, there are several research projects in which industrial by-products are used as raw materials. In turn, energy production from biomass combustion is considered to be one of the most promising energy sources. However, this type of energy produces a number of wastes that need to be treated, such as biomass bottom ash. This research evaluates the properties of biomass bottom ash for use as a filler in bituminous mixtures and quantifies the environmental advantages of its use. For this purpose, the chemical composition of the ashes was analysed and their properties were physically characterised to confirm their suitability as a filler. Subsequently, the advantages of its processing compared to limestone filler, lime, or cement were calculated with SimaPro software. The results showed acceptable properties of biomass bottom ash for use as a filler, as well as a drastic reduction in the environmental impact of its processing. In short, this research presents the basis for the development of further bituminous mixtures with biomass bottom ash, reducing the extraction of raw materials and avoiding landfill disposal.

The greater environmental awareness, new environmental regulations and the optimization of resources make possible the development of sustainable materials as substitutes for the traditional materials used in construction. In this work, geopolymers were developed as substitutes to traditional ceramics for brick manufacture, using as raw materials: chamotte, as a source of aluminosilicate, and biomass bottom ashes from the combustion of almond shell and alpeorujo (by-product produced in the extraction of olive oil composed of solid parts of the olive and vegetable fats), as the alkaline activator. For the feasibility study, samples were made of all possible combinations of both residues from 100% chamotte to 100% biomass bottom ash. The tests carried out on these sample families were the usual physical tests for ceramic materials, notably the compression strength test, as well as colorimetric tests. The freezing test was also carried out to study the in-service behavior of the different sample groups. The families with acceptable results were subjected to Fourier transform infrared (FTIR) analysis. The results of the previous tests showed that the geopolymer was indeed created for the final families and that acceptable mechanical and aging properties were obtained according to European standards. Therefore, the possibility of creating geopolymers with chamotte and biomass bottom ashes as substitutes for conventional ceramics was confirmed, developing an economical, sustainable material, without major changes in equipment and of similar quality to those traditionally used for bricks.

Mining activity produces a series of wastes that must be treated to avoid environmental pollution. In addition, some of these mining wastes still contain metallic elements that are interesting for their extraction with new less expensive techniques and that can work with low mineral grades, such as hydrometallurgy. This study evaluates the suitability of Copper recovery in mining wastes, coming from waste dump, with a high percentage of metal oxides and granite. This recovery is carried out through leaching in 0.05, 0.10, 0.15 and 0.20 molar Sulphuric Acid solutions, at ambient temperature and atmospheric pressure. The exposure of the waste to the solution was made for 96 h, taking measurements of the leaching and evaluating the increase in Copper concentration every 24 h. The results reflected a good Copper recovery rate with concentrations up to 1.9 g/L. The best results were obtained for the 0.20 molar Sulphuric Acid solutions, producing a stability in the Copper concentration after 72 h. Other elements in smaller proportion as the Zinc were also recovered. Therefore, a process of recovery of Copper was obtained with a robust, versatile and economic technique in mining residues that currently represent an environmental pollution.

Cold in-place recycling with bitumen emulsion is a good environmental option for road conservation. The technique produces lower CO2 emissions because the product is manufactured and spread in the same location as the previous infrastructure, and its mixing with bitumen emulsion occurs at room temperature. Adding materials with cementitious characteristics gives the final mixture greater resistance and durability, and incorporating an industrial by-product such as ladle furnace slag (of which cementitious characteristics have been corroborated by various authors) enables the creation of sustainable, resistant pavement. This paper describes the incorporation of ladle furnace slag in reclaimed asphalt pavements (RAP) to execute in-place asphalt pavement recycling with bitumen emulsion. Various test groups of samples with increasing percentages of emulsion were created to study both the density of the mixtures obtained, and their dry and post-immersion compressive strength. To determine these characteristics, the physical and chemical properties of the ladle furnace slag and the reclaimed asphalt pavements were analyzed, as well as compatibility with the bitumen emulsion. The aforementioned tests define an optimal combination of RAP (90%), ladle furnace slag (10%), water (2.6%), and emulsion (3.3%), which demonstrated maximum values for compressive strength of the dry and post-immersion bituminous mixture. These tests therefore demonstrate the suitability of ladle furnace slag for cold in-place recycling with bitumen emulsion.