Shape memory alloy (SMA) helical springs are special mechanical parts that require a previous evaluation of its behavior for application. Therefore, in this paper thermal and mechanical behaviour of superelastic Ni-Ti SMA helical extension springs manufactured by investment casting (IC) are evaluated. Phase transformation temperatures were measured by Electrical Resistance as a function of Temperature (ERT) and Differential Scanning Calorimetry (DSC). Tensile tests were carried out within strain and temperatures ranges. The pitch angle and stiffness of each spring were determined. Results demonstrated that Ni-Ti SMA helical springs produced by IC presented phase transformation corresponding to the superelastic effect (SE). The reversible deformations under tensile test were of the order of 70%. The mechanical behavior as function of temperature revealed a linear relationship between maximum force and spring temperature.
Este livro reúne uma seleção dos trabalhos apresentados no III Simpósio de Pós-Graduação em Engenharia Mecânica (SiPGEM), que teve como tema: "Empreendedorismo e Inovação na Pesquisa", sendo realizado na Universidade Federal de Campina Grande, em Campina Grande, Brasil, de 2 a 4 de outubro de 2019. O simpósio surgiu em 2017, por inciativa dos alunos de mestrado do Programa de Pós Graduação em Engenharia Mecânica, buscando melhorar e divulgar o programa. Assim, criou-se um evento científico local e regional, para a comunicação e divulgação da comunidade acadêmica, onde pesquisadores, pósgraduandos e graduandos são incentivados a expor seus trabalhos, palestrar e debater suas ideias. Nesta edição do evento, os trabalhos foram publicados no formato de resumo expandido, a fim de permitir que uma maior amostra do acervo científico apresentado no evento integrasse o livro. A comissão científica avaliou e selecionou ao todo vinte e dois trabalhos para compor este livro, no qual os tópicos abordados estão relacionados às principais linhas de pesquisa desenvolvidas no programa de pós-graduação em Engenharia Mecânica da UFCG: Análise e Projeto de Sistemas Termomecânicos (AST), Fenômenos de Transporte e Energia (FTE), Processos Mecânico-Metalúrgicos (PMM). Acreditamos que os vinte e dois capítulos oferecem uma boa amostra das pesquisas desenvolvidas nessas áreas dentro da nossa comunidade acadêmica local, sendo uma valorosa fonte de informações técnicas, bem como inspiração para futuras pesquisas. Por fim, agradecemos a todos que contribuíram com seus trabalhos para composição desse livro, à UAEM/UFCG, a Editora Poisson pela parceria que tornou este trabalho possível, as agências de fomento as pesquisas (CNPq, CAPES, Fapesq-PB), ás empresas parceiras e a todos os componentes da comissão organizadora do evento, cujos esforços foram essenciais para realização deste trabalho.
This paper presents a thermal and microstructural characterization of Cu 87-x Al 13 Nb x (wt%) high temperature shape memory alloys (HTSMA), with Nb contents ranging from 1 to 3%. The alloys were obtained by arc melting under argon atmosphere. Thermal characterization was performed by differential scanning calorimetry (DSC), revealing that the phase martensitic transformation of all the studied alloys occurs in the range of 200 ºC to 450 ºC. Thermal cycling in this temperature range caused the martensitic transformation to disappear after approximately 6 cycles. However, a new heat treatment at 850 ºC followed by water quenching causes the martensitic transformation to be recovered. Microstructural characterization was performed using optical microscopy (OM) and scanning electron microscopy (SEM), revealing the presence of Nb precipitates in a Cu-Al martensitic matrix, mainly in the Nb-rich compositions. These different microstructures with Nb particles cause a hardness variation that initially decreases between 0.5 %Nb (275HV) and 1.0 %Nb (225HV), then increasing continuously up to 3.0% Nb (380HV).
CDD 670.427 Elaborado por Maurício Amormino Júnior-CRB6/2422 O conteúdo dos artigos e seus dados em sua forma, correção e confiabilidade são de responsabilidade exclusiva dos autores. 2019 Permitido o download da obra e o compartilhamento desde que sejam atribuídos créditos aos autores, mas sem a possibilidade de alterá-la de nenhuma forma ou utilizá-la para fins comerciais.
Elaborado por Maurício Amormino Júnior-CRB6/2422 O conteúdo dos artigos e seus dados em sua forma, correção e confiabilidade são de responsabilidade exclusiva dos autores. 2019 Permitido o download da obra e o compartilhamento desde que sejam atribuídos créditos aos autores, mas sem a possibilidade de alterá-la de nenhuma forma ou utilizá-la para fins comerciais. www.atenaeditora.com.br APRESENTAÇÃO Caro leitor(a) Nesta obra temos um compendio de pesquisas realizadas por alunos e professores atuantes em engenharia e tecnologia. São apresentados trabalhos teóricos e vários resultados práticos de diferentes formas de aplicação e abordagens de simulação, projetos e caracterização no âmbito da engenharia e aplicação de tecnologia. Tecnologia é o pilar mais importante da engenharia. Os profissionais que se dedicam a pesquisa e desenvolvimento de novos produtos e processos não estão preocupados com todos os aspectos da tecnologia, mas com a tecnologia existente, bem como com a tecnologia futura considerada viável. Uma visão ampla de tecnologia é portando fundamental para engenheiros. É esta amplitude de áreas e temas que procuramos reunir neste livro. De abordagem objetiva, a obra se mostra de grande relevância para graduandos, alunos de pós-graduação, docentes e profissionais, apresentando temáticas e metodologias diversificadas, em situações reais Aos autores, agradecemos pela confiança e espirito de parceria. Boa leitura Franciele Bonatto
Aims:The objective was to investigate the modifications induced by grain refiners on microstructural and mechanical behaviour of Cu-Al-Be shape memory alloy. Study Design: The experiment was conducted in a completely randomized design. Place and Duration of Study: the experiment was carried out at Methodology: The alloys were prepared by induction melting and hot rolled into strips of 1.0 mm thickness at room temperature without protective atmosphere, followed of heat treatments. Subsequently the microscope analysis, differential scanning calorimetry (DSC), and mechanical Santiago et al.; CJAST, 32(4): 1-8, 2019; Article no.CJAST.46341 2 tests were carried out. Results: The shape memory alloys produced present phase transformations corresponding to the superelastic effect (SE). Grain size reduced considerably with increases content of Nb-Ni. Additionally, the mechanical tensile testing and hardness tests verified that the addition of Nb-Ni increases the stress of the alloy. Conclusion: The manufactured of Cu-Al-Be alloys by induction melting and hot rolled without protective atmosphere is viable. The microstructure analysis shows the grain refinement in Cu-Al-Be alloys containing 1.0 wt% and 1.5wt% of Nb-Ni alloy with considerable reduction in grain size. The reduction in the grain size shows the improvement in the hardness and mechanical tensile properties. Original Research Article
A proposta de melhorar a visibilidade e inserção social do Programa de Pós-Graduação em Engenharia Mecânica teve sua primeira edição em 2017, por iniciativa dos alunos de mestrado que se dedicaram, contribuíram e evoluíram para essa nova formatação, que nesse ano adotou a temática "expandindo o horizonte do jovem engenheiro". É destinado a ser um evento científico para a comunicação e divulgação da comunidade acadêmica local e regional e pretende envolver os discentes e docentes dos cursos de Graduação e Pós-Graduação em Engenharia Mecânica da UFCG e de outras IES parceiras. Tem como objetivos fomentar a integração entre alunos, a interdisciplinaridade, a divulgação dos resultados das pesquisas realizadas no âmbito das linhas de pesquisas em andamento na UFCG e colaborar na formação do pesquisador em aspectos relacionados à formação de recursos humanos de alto nível. Na sua programação inclui palestras, minicursos e seções técnicas com artigos científicos, bem como a participação de alunos de graduação, por meio das equipes de projetos de extensão (Grupos PET, ParahyBaja, Labem, Parahyasas e Scuderia), através de Stands com protótipos e painéis para divulgar os vários trabalhos em desenvolvimento na Engenharia Mecânica. Também conta com a participação de especialistas e profissionais da indústria em outras áreas trazendo novidades em temas relevantes e atuais visando motivar os alunos para a sua formação nesse ambiente acadêmico. Como parte dessa jornada tem-se buscado apoios em empresas locais e órgãos de fomento e divulgação visando aumentar o seu alcance e contribuir de maneira formal com os principais temas de pesquisa em andamento envolvendo aspectos teóricos (métodos computacionais e analíticos) e experimentais (pesquisas em laboratórios e trabalhos de campo), visando a expansão do conhecimento e potencial de aplicação de novas ferramentas com interesses compartilhados pela indústria, fortalecendo, sempre que possível, a interação da universidade com o setor produtivo. Enfim agradecemos à UAEM/UFCG e a Editora Poisson que se propôs publicar os resultados desse evento na forma de capítulos de livro, além das agências que fomentam as pesquisas (CNPq, CAPES, Fapesq-PB), às empresas parceiras e a todos os alunos de graduação e pósgraduação envolvidos, especialmente a equipe da comissão organizadora, nesse ano representada pelas alunas Raissa Alves Queiroga e Kaline Ventura Batista, pelo empenho e dedicação na formatação do livro.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.