The aim of this study is to evaluate the influence of modeling liquids on the translucency and color shade of resin composites (RCs) after one year of storage. RC specimens were prepared using either a conventional insertion technique (control; without modeling liquid) or a restorative dental modeling insertion technique (RDMIT) with dental adhesives as modeling liquids (Scotchbond ™ Multi-Purpose [SBMP; 3M ESPE] or Adper™ Single Bond 2 [SB; 3M ESPE]). The initial colors of the specimens were obtained with a digital spectrophotometer and the CIEL * a * b * color system, after which specimens were stored (37°C) in distilled water or red wine for 12 months. Color measurements were reassessed after 6 and 12 months of storage, and scanning electron microscopy was performed after 12 months. Translucency and color change (ΔE * ) were calculated and analyzed using ANOVA and Tukey's test (α = 5%). RC samples prepared via RDMIT showed a translucency similar to that of control samples. ΔE * was also less intense for RCs containing SBMP than for RCs containing SB. Specimens stored in wine showed a clear pattern of degradation, especially in the control group, and surface degradation seemed to be less intense for specimens prepared with SBMP and SB than for specimens without. Specimens stored in water did not show clear evidence of surface degradation. RDMIT appears to be an interesting approach to reduce ΔE * in RCs over time without negative effects on the translucency of the material. However, the modeling liquid should feature a hydrophobic composition, similar to that used in the SBMP group, the achieve the best results.
Modeling liquids/resins have been used to build up resin composite (RC) restorations, although there is a lack of information regarding their effects on the color stability of the latter. Therefore, the purpose of the present study was to evaluate the effects of the presence of modeling liquid between layers of RC and the finishing/polishing state of the material on color change in specimens exposed to red wine staining over time. Specimens were prepared by placing four increments (±0.5 mm thick) of RC (Filtek™ Z350 XT, 3M ESPE) into molds; half of which were prepared by applying modeling liquid (Scotchbond™ Multi-Purpose™ Adhesive, SBMP, 3M ESPE) between the layers of RC, whereas the other half were prepared without SBMP (control). Light-activation was performed after application of the final RC layer using a light-emitting diode (Radii, SDI) curing unit with an irradiance of 900 mW/cm 2 for 20 s. Each group was divided according to the surface finishing protocol (n = 7): nothing (non-polished) or polishing with Sof-Lex™/diamond paste (polished). Initial colors of the specimens were evaluated with a digital spectrophotometer and the CIEL * a * b * color system. The specimens were stored in wine (37°C) for 12 months, and the color measurements were reassessed after 4, 6, and 12 months of storage. Scanning electron microscopy (SEM) analysis was performed at the end. Data were analyzed using ANOVA and Tukey's test (α = 5%). The presence of SBMP resulted in lower overall color change of the RC as compared with the control. The non-polished specimens exhibited a significantly higher color change than the polished specimens. SEM images corroborated the previous findings. In summary, the use of modeling liquid between layers of RC shows potential for application to reduce or delay the staining process of RC over time. Moreover, polishing is essential to provide increased color stability of the RC restoration.
The aims of this study were to evaluate the effect of immediate and delayed resin cement application on the microtensile bond strength of indirect composite resin restorations and, to evaluate adhesive strategies (for regular resin cement or humidity parameters for self-adhesive resin cement). Forty-five enamel/dentin discs (0.5 mm height and 10 mm of diameter) obtained from bovine teeth were divided into nine groups (n = 5). For regular cement, the variation factors were cementation technique at three levels (immediate cementation, 5 or 30 min after adhesive system application); and type of adhesive system at two levels (three-or two-step). For self-adhesive cement, the dentin moisture was the source of variation at three levels (normal, dry, or wet cementation). The specimens were submitted to microtensile bond strength (μTBS) testing using a universal testing machine. Data were analyzed by ANOVA, Tukey's test, and linear regression. Regular cement and three-step etch-and-rinse adhesive system showed the highest values of bond strength (25.21 MPa-30 min of delay). Only for this condition, three-step adhesive showed higher bond strength than the two-step adhesive. Nevertheless, the linear regression showed that irrespective of the strategy, the use of the two-step approach when compared with three-step adhesive system decreased μTBS (p < 0.001). The failure analysis showed predominant adhesive failures for all tested groups. All groups had comparable values of bond strength to bovine dentin when the same materials were used, even in suboptimal clinical conditions.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.