Cycloaddition. -Significant amounts (20-45% NMR) of undesired regioisomers are also generated in some cases. -(MORI, A.; ARAKI, T.; MIYAUCHI, Y.; NOGUCHI, K.; TANAKA*, K.; Eur.

No abstract

A novel series of linear, high-molecular-weight polymers and copolymers was synthesized by one-pot, metal-free superacid-catalyzed reaction of trifluoromethylalkyl (1a−1c) and trifluoromethylaryl (1d−1h) ketones with the linear, nonactivated, multiring aromatic hydrocarbons biphenyl (A), p-terphenyl (B), and p-quaterphenyl (C). The polymerizations were performed at room temperature in the Brønsted superacid trifluoromethanesulfonic acid (CF 3 SO 3 H, TFSA) and in a mixture of TFSA with methylene chloride. Polymerizations of trifluoromethyl ketones (1c, 1f−1h) bearing functional groups gave polymers with reactive lateral groups such as bromomethyl, 4-(N,N-dimethylamino)phenyl-, 3-sulfophenyl-, and 2,3,4,5,6-pentafluorophenyl. The polymers obtained were soluble in most common organic solvents and flexible transparent films could be cast from the solutions. 1 H and 13 C NMR analyses of the polymers synthesized revealed their linear structure with para-substitution in the phenylene fragments of the main chain. The molecular weights (M w ) of the polymers based on trifluoromethylalkyl ketones and aromatic are very high and reach 1 000 000, while the molecular weights of the polymers based on trifluoromethylaryl ketones and aromatic ranged from 30 000 to 300 000 g/mol. The polydispersity of the polymers is generally less than 2. The polymers also possess high thermostability. Mechanistic aspects of polymerization mechanism have been discussed, and a new approach for monomer design has been proposed.

A novel series of linear, high-molecular-weight polymers was synthesized by one-pot, metalfree superacid-catalyzed reaction of isatins (1a-d) with linear, nonactivated, multiring aromatic hydrocarbons: biphenyl (A), p-terphenyl (B), p-quaterphenyl (C), 2-(4-biphenylyl)-6-phenylbenzoxazole (D), 9Hfluorene (E), 9,9-dimethyl-9H-fluorene (F), 2,2 0 -[2,5-bis(trifluoromethyl)-1,4-phenylene]bis(9,9-dimethyl-9H-fluorene) (G), oligo-9,9-bis(2,6-ethylhexyl)-9H-fluorene (H), biphenol (I), and bi-2-napththol (J). The reactions were performed at room temperature in the Brønsted superacid trifluoromethanesulfonic acid (CF 3 SO 3 H, TFSA) and in a mixture of TFSA with methylene chloride or TFA tolerant of hydroxyl, carboxy, and cyano groups. The polymers obtained were soluble in most common organic solvents, and flexible transparent films could be cast from the solutions. 1 H and 13 C NMR analyses of the polymers synthesized revealed their linear structure with para-substitution in the phenylene fragments of the main chain. The molecular weights M w and M n of the polymers ranged from 54200 to 742000 and from 40140 to 438500 g/mol, respectively. Most of the polymers also possess narrow polydispersity (1.15-1.50). The oxindole groups of the polymers react smoothly with alkyl bromides under basic conditions in N-methylpyrrolidinone (NMP). The amount of "click"able allyl-and propargyl-functionalities is readily controlled by adjusting the reaction ratio of polymer to alkyl bromides. The demonstrated efficiency and orthogonality of isatin-based polymer chemistry shows it to be an essential addition to the family of polymer "click" reactions.

This report presents a general overview of non-stoichiometric step-growth polymerizations (polycondensations). Three kinds of non-stoichiometric polycondensations are defined and discussed for a(2) + b(2) monomer combinations. Depending on the kinetic scenario and on the experimental conditions, the excess of one monomer either strongly reduces or strongly enhances the average degree of polymerization (DP) relative to a stoichiometric polycondensation under identical conditions. As a result, telechelic oligomers or extremely high molar mass polymers (DPs > 1000) may be formed. Stoichiometric imbalance has in all cases the consequence that cyclization is largely suppressed in early stages of a polycondensation. Finally, non- stoichiometric "a(2) + b(n) " polycondensations are discussed.