Uranium dioxide (UO2), the primary fuel for commercial nuclear reactors, incorporates excess oxygen forming a series of hyperstoichiometric oxides. Thin layers of these oxides, such as UO2.12, form readily on the fuel surface and influence its properties, performance, and potentially geologic disposal. This work reports a rapid and straightforward combustion process in uranyl nitrate–glycine–water solutions to prepare UO2.12 nanomaterials and thin films. We also report on the investigation of the structural changes induced in the material by irradiation. Despite the simple processing aspects, the combustion synthesis of UO2.12 has a sophisticated chemical mechanism involving several exothermic steps. Raman spectroscopy and single-crystal X-ray diffraction (XRD) measurements reveal the formation of a complex compound containing the uranyl moiety, glycine, H2O, and NO3 – groups in reactive solutions and dried combustion precursors. Combustion diagnostic methods, gas-phase mass spectroscopy, differential scanning calorimetry (DSC), and extracted activation energies from DSC measurements show that the rate-limiting step of the process is the reaction of ammonia with nitrogen oxides formed from the decomposition of glycine and uranyl nitrate, respectively. However, the exothermic decomposition of the complex compound determines the maximum temperature of the process. In situ transmission electron microscopy (TEM) imaging and electron diffraction measurements show that the decomposition of the complex compound directly produces UO2. The incorporation of oxygen at the cooling stage of the combustion process is responsible for the formation of UO2.12. Spin coating of the solutions and brief annealing at 670 K allow the deposition of uniform films of UO2.12 with thicknesses up to 300 nm on an aluminum substrate. Irradiation of films with Ar2+ ions (1.7 MeV energy, a fluence of up to 1 × 1017 ions/cm2) shows unusual defect-simulated grain growth and enhanced chemical mixing of UO2.12 with the substrate due to the high uranium ion diffusion in films. The method described in this work allows the preparation of actinide oxide targets for fundamental nuclear science research and studies associated with stockpile stewardship.
Combustion synthesis in uranyl nitrate–acetylacetone–2-methoxyethanol solutions was used to deposit thin UO2 films on aluminum substrates to investigate the irradiation-induced restructuring processes. Thermal analysis revealed that the combustion reactions in these solutions are initiated at ∼160 °C. The heat released during the process and the subsequent brief annealing at 400 °C allow the deposition of polycrystalline films with 5–10 nm UO2 grains. The use of multiple deposition cycles enables tuning of the film thicknesses in the 35–260 nm range. Irradiation with Ar2+ ions (1.7 MeV energy and a fluence of up to 1 × 1017 ions/cm2) is utilized to generate a uniform distribution of atomic displacements within the films. X-ray fluorescence (XRF) and alpha-particle emission spectroscopy showed that the films were stable under irradiation and did not undergo sputtering degradation. X-ray photoelectron spectroscopy (XPS) showed that the stoichiometry and uranium ionic concentrations remain stable during irradiation. The high-resolution electron microscopy imaging and electron diffraction analysis demonstrated that at the early stages of irradiation (below 1 × 1016 ion/cm2) UO2 films show complete amorphization and beam-induced densification (sintering), resulting in a pore-free disordered film. Prolonged irradiation (5 × 1016 ion/cm2) is shown to trigger a crystallization process at the surface of the films that moves toward the UO2/Al interface, converting the entire amorphous material into a highly crystalline film. This work reports on an entirely different radiation-induced restructuring of the nanoscale UO2 compared to the coarse-grained counterpart. The preparation of thin UO2 films deposited on Al substrates fills an area of national need within the stockpile stewardship program of the National Nuclear Security Administration and fundamental research with actinides. The method reported in this work produces pure, robust, and uniform thin-film actinide targets for nuclear science measurements.
A simple and efficient target preparation method is developed combining spin coating and solution combustion synthesis. Multiple smooth and uniform UO2 targets have been prepared using this method on a variety of backings (aluminium, carbon, silicon) used in nuclear physics experiments. The thicknesses of the targets can be precisely tuned by changing the number of coatings within the range of ~50-1000 µm/cm2. These targets are highly uniform (<5% deviation), robust, and remain strongly adherent to their backings even after being irradiated by high doses (1017 ions/ cm2) of 1.7 MeV Ar2+ ions.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.