Catalysis is at the core of almost every established and emerging chemical process and also plays a central role in the quest for novel technologies for the sustainable production and conversion of energy. Particularly since the early 2000s, a great surge of interest exists in the design and application of micro- and nanometer-sized materials with hollow interiors as solid catalysts. This review provides an updated and critical survey of the ever-expanding material architectures and applications of hollow structures in all branches of catalysis, including bio-, electro-, and photocatalysis. First, the main synthesis strategies toward hollow materials are succinctly summarized, with emphasis on the (regioselective) incorporation of various types of catalytic functionalities within their different subunits. The principles underlying the scientific and technological interest in hollow materials as solid catalysts, or catalyst carriers, are then comprehensively reviewed. Aspects covered include the stabilization of catalysts by encapsulation, the introduction of molecular sieving or stimuli-responsive "auxiliary" functionalities, as well as the single-particle, spatial compartmentalization of various catalytic functions to create multifunctional (bio)catalysts. Examples are also given on the applications which hollow structures find in the emerging fields of electro- and photocatalysis, particularly in the context of the sustainable production of chemical energy carriers. Finally, a critical perspective is provided on the plausible evolution lines for this thriving scientific field, as well as the main practical challenges relevant to the reproducible and scalable synthesis and utilization of hollow micro- and nanostructures as solid catalysts.

This study focuses on the synthesis and electrochemical performance (i.e, activity and stability) of advanced electrocatalysts for the oxygen reduction reaction (ORR), made of Pt–Ni nanoparticles embedded in hollow graphitic spheres (HGS). The mechanism of the confined space alloying, that is, the controlled alloying of bimetallic precursors with different compositions (i.e., Pt3Ni, PtNi, and PtNi3) within the HGS mesoporous shell, was examined in detail. It was found that the presence of platinum during the reduction step, as well as the application of high annealing temperatures (at least 850 °C for 3.5h in Ar), are necessary conditions to achieve the complete encapsulation and the full stability of the catalysts. The evolution of the activity, the electrochemical surface area, and the residual alloy composition of the Pt–Ni@HGS catalysts was thoroughly monitored (at the macro- and nanoscale level) under different degradation conditions. After the initial activation, the embedded Pt–Ni nanoparticles (3–4 nm in size) yield mass activities that are 2- to 3.5-fold higher than that of pure Pt@HGS (depending on the alloy composition). Most importantly, it is demonstrated that under the normal operation range of an ORR catalyst in PEM-FCs (potential excursions between 0.4 and 1.0 VRHE) both the nanoparticle-related degradation pathways (particle agglomeration) and dealloying phenomena are effectively suppressed, irrespectively of the alloy composition. Thus, the initial enhanced activity is completely maintained over an extended degradation protocol. In addition, owing to the peculiar configuration of the catalysts consisting of space-confined nanoparticles, it was possible to elucidate the impact of the dealloying process (as a function of alloy composition and severity of the degradation protocols) separately from other parallel phenomena, providing valuable insight into this elusive degradation mechanism.

No abstract

The performance of polymer electrolyte fuel cells is strongly correlated to the electrocatalytic activity and stability. In particular, the latter is the result of an interplay between different degradation mechanisms. The essential high stability, demanded for real applications, requires the synthesis of advanced electrocatalysts that withstand the harsh operation conditions. In the first part of this study, the synthesis of oxygen reduction electrocatalysts consisting of Pt-Co (i.e., Pt5Co, Pt3Co, and PtCo) alloyed nanoparticles encapsulated in the mesoporous shell of hollow graphitic spheres (HGS) is reported. The mass activities of the activated catalysts depend on the initial alloy composition and an activity increase on the order of two to threefold, compared to pure Pt@HGS, is achieved. The key point of the second part is the investigation of the degradation of PtCo@HGS (showing the highest activity). Thanks to pore confinement, the impact of dissolution/dealloying and carbon corrosion can be studied without the interplay of other degradation mechanisms that would induce a substantial change in the particle size distribution. Therefore, impact of the upper potential limit and the scan rates on the dealloying and electrochemical surface area evolution can be examined in detail