The voiding behavior of mixed solder alloy systems during BGA assembly was investigated with the use of nitrogen reflow atmosphere. The solder joints were comprised of a combination of Sn62Pb36Ag2 (Sn62), Sn63Pb37 (Sn63), Sn98.5Ag1Cu0.5 (SAC105), and Sn96.5Ag3Cu0.5 (SAC305) as the solder ball or solder paste, except for SnPb solder balls with lead-free pastes. Assembly of each BGA employed a high temperature (HT) profile for lead-free and mixed systems, and a low temperature (LT) profile for mixed and SnPb systems. Mixed systems had higher voiding than lead-free systems when reflowed at HT. SnPb systems had a wider voiding range when compared with mixed systems reflowed at LT. Voiding was found to decrease with reduced alloy surface tension, earlier melting of the bottom solder paste, the top ball remaining solid during reflow, a narrower pasty range, smaller joint overheating, and using flux alone instead of solder paste.
Low melting 57Bi42Sn1Ag (BiSnAg) was explored for replacing SAC solders as a low-cost solution. In this study, BGAs with SAC105, SAC305, and BiSnAg balls were assembled with SAC105, SAC305 or 57Bi42Sn1Ag solder paste. Joint mechanical strength, drop test performance, and voiding performance were evaluated against the reflow profile. SnPb was included as a control. The findings are as follows: (1) The microstructure of solder joints showed that, among all of the combinations, only BiSnAg-105 LT and BiSnAg-305 LT exhibited well-distinguishable alloy regions. For SAC-BiSnAg systems, Sn-dendrites were noticeable at LT, while Ag3Sn needles developed at HT. The joints were homogeneous for the rest of the combinations. (2) In the shear test, combinations involving BiSnAg solder were brittle, regardless of the Bi alloy location and reflow profile, as evidenced by stress-strain curves and morphology of the ruptured surface. The strong influence of Bi on the rupture site may have been caused by the stiffening effect of solder due to the homogenized presence of Bi in the joint. With the stiffened solder, the brittle IMC interface became the weakest link upon shearing, although the brittle BiSn crystalline structure also contributed to the rupture. (3) In the drop test, all Bi-containing solder joints performed poorly compared with Bi-free systems, which was consistent with shear test results. Drop numbers increased with increasing elongation at break of solder bumps as measured in the shear test. (4) Voiding was affected by flux chemistry and reduced by low alloy homogenization temperatures and solid top factors, but was increased by low surface tension factor, melting sequence factor, overheating factor and wide pasty range factor. Compared to SAC or SnPb systems, the BiSnAg system is low in voiding if reflowed at LT. In this study, voiding had an insignificant effect on shear strength and drop test performance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.