The aim of this study is to describe the remineralization effect of the nano-HA toothpaste on artificial caries. The artificial dental caries is made using sour solution. The demineralized teeth specimen is put into five kinds of toothpaste solution respectively for 5 days and 10 days, which are: solution of containing needle like nano-HA, solution of containing spherical nano-HA, solution of general HA, fluorine sodium solution and physiological saline. The hardness of specimen is measured and the surface morphology is characterized by SEM. The remineralized test indicates that the nano-HA toothpaste can enhance the hardness of artificial caries and improve the remineralization of artificial caries. The SEM analysis shows that the cavities and defects of enamel surface are decreased and many mineral salts are sedimentated, which indicate that the nano-HA could promote remineralization for the demineralized enamel.
The purpose of this study is to examine the inhibitory effects of nano-HA on the caries-inducing properties of a four-organism bacterial consortium in vitro. A series of in vitro anticarious experiments have been carried out by using a continuous culture system. Streptococcus mutans, Streptococcus sanguis, Actinomyces viscosus, Lactobacillus rhamnosus have been chosen as the experimental bacteria. After 48 hours, the dental plaque surface structure is observed with the scan electron microscope and the bacterial colonization was evaluated on dental plaque. The results show that Spherical nano-HA and mixed nano-HA are proved to be effective in anticarious experiments, and especially spherical nano-HA is more striking. It is able to damage the formation of biofilms (dental plaque), postpone or end the process of acid generation of bacteria metabolism. After 7 days, the demineralization of the enamel has been detected by using TEM. The spherical nano-HA might have a remineralization to early caries to prevent and decrease caries.
The objective of this study was to investigate the inhibitory effect of the synthetic nanohydroxyapatite (HA) on dental caries. The nano-HA was synthesized by using the depositing reaction of Ca (H2PO4)2. The artificial dental caries was made by using sour solution and inoculating Streptococcus mutans (S.mutans) to the Sprague-Dawley (SD) rat’s mouth respectively. After mineralization of solution of nano-HA for 10 days, the hardness of enamel was measured. The inhibitory effect of the synthetic nano-HA on dental caries was detected by gargling way to rinse the rat tooth with the solution of nano-HA in the animal test. Transmission electron microscopy (TEM) revealed that the dried HA particles were needle-like with ф5-20nm×60nm and the sintered HA particles were spherical with less than 100nm. The remineralized test indicated that the solution of nano-HA with different shapes enhanced the hardness of artificial caries and improved the remineralization of artificial caries. The animal test showed that the dried nano-HA had the inhibitory effect on dental caries. The good absorptive effect of the nano-HA on both the saliva protein and the glucans leads to the development of interventions that could reduce or modify bacterial colonization of tooth surfaces.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.