The thick plate narrow gap welding of 25Cr2NiMo1V rotor steel is achieved by metal active gas arc welding, in which the weld gap was 18.04–19.9 mm. After welding, the weldment was heat treated at 580 °C (20 h). The impact and tensile properties in the as-welded and heat-treated were studied. The results show that after heat treatment, the coarse carbides in the center of the weld were transformed into fine granular carbides distributed along the grain boundaries, and the quantity of carbide precipitates in the weld near the fusion line was reduced. The tensile fracture mode changed from a ductile fracture to a combination of brittle and ductile fractures, and the tensile strength of the weld metal changed from 605 MPa to 543 MPa. After heat-treated, the radiation zone of the weld center changed from a brittle fracture to a combination of brittle and ductile fractures, and the impact energy changed from 141 J to 183 J; the characteristics of the brittle fracture in the radial zone of the fusion line were more obvious, and the impact energy changed from 113 J to 95 J. Therefore, after heat treatment, the toughness of the welded metal was improved, without reducing the strength and hardness of the welded metal to a large extent.
The narrow gap MAG welding system was used to successfully weld the 50mm thick butt joint of 25Cr2NiMo1V rotor steel. After 15-layer bead welding, heat treatment is performed on the welded joint. Compare the changes in the microstructure, tensile strength and impact energy of the welded joints and the heat-treated joints at 580°C (20h). The results show that after the heat treatment of the structure, the side lath ferrite in the coarse-grained region grows up, and the eutectoid ferrite grows up in the fine-grained region first. The strength of the welded joint is about 605MPa, and the fracture is characterized by ductile fracture. After heat treatment at 580°C (20h), the strength is about 543MPa, the fracture is characterized by ductile fracture, and there are also a large number of discontinuous small surface platforms, and the characteristic of brittle fracture appears slightly. The impact energy of the weld center of the welded joint is about 141J, the fusion line area is about 113J, and the toughness of the fusion line is slightly lower than that of the weld center. After heat treatment, the impact energy at the center of the weld is about 183J, the fusion line area is about 95J, the toughness of the weld center increases, and the toughness of the fusion line decreases.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.