Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV), a biodegradable polyester, has been a good candidate of biomaterial employed in tissue engineering. However, the PHBV film is hydrophobic and has no recognition sites for cell attachment. In this study, PHBV films are activated by ammonia plasma treatment to produce amino groups on the surface, followed by sequential reactions with a heterobifunctional cross-linker containing a segment of poly(ethylene glycol) (PEG) and further with RGD-containing peptides. XPS analyses of modified surfaces after each reaction step reveal that the RGD-containing peptides have been covalently grafted onto PHBV films. The result of cell viability assay indicates that the RGD-modified PHBV films exhibit a distinctly improved cellular compatibility. Moreover, according to the results of serum adsorption tests by optical waveguide lightmode spectroscopy (OWLS) and fibrinogen adsorption tests by enzyme-linked immunosorbent assay (ELISA) on unmodified and modified PHBV surfaces, the introduced PEG chains can significantly decrease the nonspecific adsorption of proteins from serum and fibrinogen from plasma, thus decreasing the risk of thrombus formation and improving the blood compatibility of implanted materials.
Mesoporous anatase-phase TiO2 hollow shells were successfully fabricated by the solvothermal and calcination process. This method involves preparation of SiO2@TiO2 core-shell colloidal templates, sequential deposition of carbon and then silica layers through solvothermal and sol-gel processes, crystallization of TiO2 by calcination and finally removal of the inner and outer silica to produce hollow anatase TiO2 shells. The prepared samples were characterized by transmission electron microscopy, X-ray diffraction, N2 adsorption-desorption isotherms and UV-vis absorption spectroscopy. The results show that a uniform carbon layer is coated on the core-shell particles through the solvothermal process. The combustion of carbon offers the space for the TiO2 to further grow into large crystal grains, and the outer silica layer serves as a barrier against the excessive growth of anatase TiO2 nanocrystals. Furthermore, the initial crystallization of TiO2 generated in the carbon coating step and the heat generated by the combustion of the carbon layer allow the crystallization of TiO2 at a relatively low temperature without changing the uniform structure. When used as photocatalysts for the oxidation decomposition of Rhodamine B in aqueous solution under UV irradiation, the hollow TiO2 shells showed enhanced catalytic activity. Moreover, the TiO2 hollow shells prepared with optimal crystallinity by this method showed a higher performance than commercial P25 TiO2.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.