Sodium-ion batteries (SIBs) are still confronted with several major challenges, including low energy and power densities, short-term cycle life, and poor low-temperature performance, which severely hinder their practical applications. Here, a high-voltage cathode composed of Na V (PO ) O F nano-tetraprisms (NVPF-NTP) is proposed to enhance the energy density of SIBs. The prepared NVPF-NTP exhibits two high working plateaux at about 4.01 and 3.60 V versus the Na /Na with a specific capacity of 127.8 mA h g . The energy density of NVPF-NTP reaches up to 486 W h kg , which is higher than the majority of other cathode materials previously reported for SIBs. Moreover, due to the low strain (≈2.56% volumetric variation) and superior Na transport kinetics in Na intercalation/extraction processes, as demonstrated by in situ X-ray diffraction, galvanostatic intermittent titration technique, and cyclic voltammetry at varied scan rates, the NVPF-NTP shows long-term cycle life, superior low-temperature performance, and outstanding high-rate capabilities. The comparison of Ragone plots further discloses that NVPF-NTP presents the best power performance among the state-of-the-art cathode materials for SIBs. More importantly, when coupled with an Sb-based anode, the fabricated sodium-ion full-cells also exhibit excellent rate and cycling performances, thus providing a preview of their practical application.
A novel core-shell FeO@FeS composed of FeO core and FeS shell with the morphology of regular octahedra has been prepared via a facile and scalable strategy via employing commercial FeO as the precursor. When used as anode material for sodium-ion batteries (SIBs), the prepared FeO@FeS combines the merits of FeS and FeO with high Na-storage capacity and superior cycling stability, respectively. The optimized FeO@FeS electrode shows ultralong cycle life and outstanding rate capability. For instance, it remains a capacity retention of 90.8% with a reversible capacity of 169 mAh g after 750 cycles at 0.2 A g and 151 mAh g at a high current density of 2 A g, which is about 7.5 times in comparison to the Na-storage capacity of commercial FeO. More importantly, the prepared FeO@FeS also exhibits excellent full-cell performance. The assembled FeO@FeS//NaV(PO)OF sodium-ion full battery gives a reversible capacity of 157 mAh g after 50 cycles at 0.5 A g with a capacity retention of 92.3% and the Coulombic efficiency of around 100%, demonstrating its applicability for sodium-ion full batteries as a promising anode. Furthermore, it is also disclosed that such superior electrochemical properties can be attributed to the pseudocapacitive behavior of FeS shell as demonstrated by the kinetics studies as well as the core-shell structure. In view of the large-scale availability of commercial precursor and ease of preparation, this study provide a scalable strategy to develop advanced anode materials for SIBs.
Graphene incorporation should be one effective strategy to develop advanced electrode materials for a sodium-ion battery (SIB). Herein, the micro/nanostructural Sb/graphene composite (Sb-O-G) is successfully prepared with the uniform Sb nanospheres (∼100 nm) bound on the graphene via oxygen bonds. It is revealed that the in-situ-constructed oxygen bonds play a significant role on enhancing Na-storage properties, especially the ultrafast charge/discharge capability. The oxygen-bond-enhanced Sb-O-G composite can deliver a high capacity of 220 mAh/g at an ultrahigh current density of 12 A/g, which is obviously superior to the similar Sb/G composite (130 mAh/g at 10 A/g) just without Sb-O-C bonds. It also exhibits the highest Na-storage capacity compared to Sb/G and pure Sb nanoparticles as well as the best cycling performance. More importantly, this Sb-O-G anode achieves ultrafast (120 C) energy storage in SIB full cells, which have already been shown to power a 26-bulb array and calculator. All of these superior performances originate from the structural stability of Sb-O-C bonds during Na uptake/release, which has been verified by ex situ X-ray photoelectron spectroscopies and infrared spectroscopies.
As a promising alternative for lithium ion batteries, room-temperature sodium ion batteries (SIBs) have become one significant research frontier of energy storage devices although there are still many difficulties to be overcome. For the moment, the studies still concentrate on the preparation of new electrode materials for SIBs to meet the applicability. Herein, one new P2-Na2/3Ni1/3Mn5/9Al1/9O2 (NMA) cathode material is successfully prepared via a simple and facile liquid-state method. The prepared NMA is layered transition metal oxide, which can keep stable crystal structure during sodiation/desodiation as demonstrated by the ex situ X-ray diffraction, and its electrochemical properties can be further enhanced by connecting the cake-like NMA microparticles with reduced graphene oxide (RGO) using a ball milling method. Electrochemical tests show that the formed RGO-connected NMA (NMA/RGO) can deliver a higher reversible capacity of up to 138 mAh g(-1) at 0.1 C and also exhibit a superior high-rate capabilities and cycling stability in comparison to pure NMA. The much improved properties should be attributed to the reduced particle size and improvement of electrical conductivity and apparent Na(+) diffusion due to RGO incorporation, which is comprehensively verified by the electrochemical technologies of galvanostatic intermittent titration technique, electrochemical impedance spectroscopy and cyclic voltammetry at various scan rate as well as ex-situ X-ray diffraction studies.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.