LiNi0.5Mn1.5−xSnxO4 (0 ≤ x ≤ 0.1) cathode materials with uniform and fine particle sizes were successfully synthesized by a two-step calcination of solid-state reaction method. As the cathode materials for lithium ion batteries, the LiNi0.5Mn1.48Sn0.02O4 shows the highest specific capacity and cycle stability. In the potential range of 3.5-4.9 V at room temperature, LiNi0.5Mn1.48Sn0.02O4 composite material shows a discharge capacity of more than 117 mA h g −1 at 0.1 C, while the corresponding discharge capacity of undoped LiNi0.5Mn1.5O4 is only 101 mA h g −1 . Moreover, in cycle performance, all the LiNi0.5Mn1.5−xSnxO4 (0 ≤ x ≤ 0.1) samples show better capacity retention than the undoped LiNi0.5Mn1.5O4 at 1 C rate after 100 cycles. Especially, for the LiNi0.5Mn1.5O4, the discharge capacity after 100 cycles is 90 mA h g −1 , while the corresponding discharge capacities of the undoped LiNi0.5Mn1.5O4 is only 56.1 mA h g −1 . The significantly enhanced DLi + and the enlarged electronic conductivity make the Sn-doped spinel LiNi0.5Mn1.5O4 material present even more excellent electrochemical performances. These results reveal that Sn-doping is an effective way to improve electrochemical performances of LiNi0.5Mn1.5O4.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.