How to significantly improve the mechanical and tribological properties of polyamide 46/polyphenylene oxide (PA46/PPO) alloy is an urgent but challenging issue. The PA46/PPO alloy reinforced with polyurethane-coated carbon fiber (PCF) was prepared and characterized. It was found that the mechanical properties, heat resistance, and tribological properties of PA46/PPO were greatly enhanced by incorporating PCF. When the composite containing 40 wt% of PCF, the tensile strength of the composite increased from 82 MPa to 282 MPa; meanwhile, volumetric wear was 0.56 mm3, which decreased by 95% in comparison with PA46/PPO. Scanning electron microscopy results showed that PCF had a good compatibility with the polymer matrix, due to good interfacial interaction between the PCF and the PA46/PPO. X-Ray photoelectron spectroscopy and laser Raman spectroscopy results further revealed that more graphitic carbon was microcracked to form a lubricating layer during friction process, thus remarkably improving the wear resistance of PA46/PPO.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.