Chemically tuned inorganic-organic hybrid materials, based on CH3NH3(═MA)Pb(I(1-x)Br(x))3 perovskites, have been studied using UV-vis absorption and X-ray diffraction patterns and applied to nanostructured solar cells. The band gap engineering brought about by the chemical management of MAPb(I(1-x)Br(x))3 perovskites can be controllably tuned to cover almost the entire visible spectrum, enabling the realization of colorful solar cells. We demonstrate highly efficient solar cells exhibiting 12.3% in a power conversion efficiency of under standard AM 1.5, for the most efficient device, as a result of tunable composition for the light harvester in conjunction with a mesoporous TiO2 film and a hole conducting polymer. We believe that the works highlighted in this paper represent one step toward the realization of low-cost, high-efficiency, and long-term stability with colorful solar cells.

Organic-inorganic hybrid perovskites are emerging low-cost emitters with very high color purity, but their low luminescent efficiency is a critical drawback. We boosted the current efficiency (CE) of perovskite light-emitting diodes with a simple bilayer structure to 42.9 candela per ampere, similar to the CE of phosphorescent organic light-emitting diodes, with two modifications: We prevented the formation of metallic lead (Pb) atoms that cause strong exciton quenching through a small increase in methylammonium bromide (MABr) molar proportion, and we spatially confined the exciton in uniform MAPbBr3 nanograins (average diameter = 99.7 nanometers) formed by a nanocrystal pinning process and concomitant reduction of exciton diffusion length to 67 nanometers. These changes caused substantial increases in steady-state photoluminescence intensity and efficiency of MAPbBr3 nanograin layers.

No abstract

Bright organic/inorganic hybrid perov-skite light-emitting diodes (PrLEDs) are realized by using CH3 NH3 PbBr3 as an emitting layer and self-organized buffer hole-injection layer (Buf-HIL). The PrLEDs show high luminance, current efficiency, and EQE of 417 cd m(-2) , 0.577 cd A(-1) , and 0.125%, respectively. Buf-HIL can facilitate hole injection into CH3 NH3 PbBr3 as well as block exciton quenching.

The inverted CH3NH3PbI3 planar hybrid solar cells exhibited better device efficiency and stability and lower hysteresis than the normal cells.

A power conversion efficiency of 10.4% is demonstrated in planar CH3 NH3 PbBr3 hybrid solar cells without hysteresis of the J-V curve, by way of controlled crystallization in the spin-coating process. The high efficiency is attributed to the formation of a dense CH3 NH3 PbBr3 thin film by the introduction of HBr solution because the HBr increases the solubility of the CH3 NH3 PbBr3 and forms a thinner CH3 NH3 PbBr3 layer with full surface coverage.

Readily commercializable and cost-effective next-generation CsPbBr perovskite nanocrystals (PNCs) based X-ray detectors are demonstrated. The PNCs-based X-ray detector exhibits higher spatial resolution (9.8 lp mm at modulation transfer function (MTF) = 0.2 and 12.5-8.9 lp mm for a linear line chart), faster response time (≈200 ns), and comparable stability (>40 Gy s of X-ray exposure) compared with the commercialized terbium-doped gadolinium oxysulfide (GOS)-based detectors (spatial resolution = 6.2 lp mm at MTF = 0.2 and 6.3 lp mm for a linear line chart, response time = ≈1200 ns) because the PNCs-based scintillator has ≈5.6-fold faster average photoluminescence lifetime and stronger emission than the GOS-based one.

No abstract