The aim of this study was to compare the physicochemical properties, filling ability, and antibacterial activity of a premixed calcium silicate-based sealer to those of a powder–liquid bioceramic sealer. Ceraseal (CS) and BioRoot (BR) materials were analyzed using scanning electron microscopy and energy-dispersive X-ray spectroscopy at 7 and 14 d of immersion in distilled water. The filling ability of the two sealers as well as the water contact angle, solubility, flow, roughness, crystalline microstructure, pH, and compressive strength were also evaluated. The antibacterial activity was assessed through an agar diffusion as well as through direct tests. All the results were statistically analyzed using one-way or two-way analysis of variance tests. Statistically significant lower void percentages were observed for CS at 2 and 8 mm from the working length (WL) compared to those for the BR group, whilst no significant difference was observed at 5 mm from the WL. BR sealer showed higher alkaline pH, rougher surface, lower water contact angle values, lower flowability, and higher solubility compared to CS. BR showed globular and needle-like crystalline microstructure, whilst CS had globular and flower-like crystalline microstructure up to 72 h. No statistical difference was found for the compressive strength between the two sealers. BR and CS showed no antibacterial effect against Enterococcus faecalis after 3 h, whilst both sealers showed antibacterial capacity after 24 and 72 h. BR demonstrated higher antibacterial activity after 24 h. In conclusion, the use of bioceramic sealers may play an important role in controlling bacterial growth. Moreover, CS may have superior filling ability and lower solubility than the BioRoot sealer due to its specific chemical composition and mixing method.
(1) Background: This study investigated the effect of the adhesive layer thickness and the length of resin tags on dentin bond strength of five universal adhesives applied in self-etch mode. (2) Methods: One hundred and fifty extracted human third molars were used. Five different universal adhesives were applied in self-etch mode on the dentin surface. Half of the specimens were subjected to an aging procedure for six months. A shear bond strength (SBS) test was performed and the results were statistically analyzed with a t-test and one-way ANOVA test. Scanning electron microscopy (SEM) was executed to measure the adhesive layer thickness and tag depth. (3) Results: No statistical differences were found between the five adhesive systems after a 24 h storage period, regardless of layer thickness and tag depth (p < 0.05). After 6 months of aging in water at 37 °C, Iperbond Max and Scotchbond Universal preserved the bond strength over time (p < 0.05), whilst the SBS of Iperbond Ultra, FuturaBond M+, and Ibond Universal decreased significantly after the aging period. No relation was observed between the adhesive thickness or tags’ length on SBS. (4) Conclusions: Within the limitation of this study, the stability over time of the bond strength of universal adhesives depends on their compositions regardless of the adhesive layer thickness and/or tags’ length.
The purpose of the present study was to evaluate the physicochemical properties and antibacterial activity of three calcium silicate cements. Mineral trioxide aggregate (MTA Biorep “BR”), Biodentine (BD) and Well-Root PT (WR) materials were investigated using scanning electron microscopy (SEM) at 24, 72 and 168 h of immersion in phosphate buffered saline (PBS). The antibacterial activity against Enterococcus faecalis (E.faecalis), the solubility, roughness, pH changes and water contact angle were also analyzed. All results were statistically analyzed using a one-way analysis of variance test. Statistically significant lower pH was detected for BD than WR and BR (p < 0.05). No statistical difference was found among the three materials for the efficacy of kill against E. faecalis (p > 0.05). Good antibacterial activity was observed (kill 50% of bacteria) after 24 h of contact. The wettability and the roughness of BR were higher than for the other cements (p < 0.05). BD was more soluble than WR and BR (p < 0.05). In conclusion, the use of bioceramic cements as retrograde materials may play an important role in controlling bacterial growth and in the development of calcium phosphate surface layer to support healing. Moreover, the premixed cement was easier to use than powder–liquid cement.
HAL is a multidisciplinary open access archive for the deposit and dissemination of scientific research documents, whether they are published or not. The documents may come from teaching and research institutions in France or abroad, or from public or private research centers. L'archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau recherche, publiés ou non, émanant des établissements d'enseignement et de recherche français ou étrangers, des laboratoires publics ou privés.
The aim of the present in vitro study was to evaluate specific mechanical and physicochemical properties of two calcium silicate based sealers, (AH Plus Bioceramic “AHPB”; Well-Root ST “WRST”), and a conventional resin sealer (AH Plus “AHP”). These aims were accomplished by assessing the porosity, pH, compression strength, roughness, wettability and cell attachment of the tested materials. The results were compared statistically using the one-way ANOVA test. Higher pH values were obtained in both AHPB and WRST compared to AHP at 3, 24 and 72 h (p < 0.05). A greater level of porosity and wettability was detected for both AHPB and WRST compared to the resin sealer AHP (p < 0.05). Evident cell growth characterized by elongated morphology was observed on the surface of AHPB and WRST, while only a thin layer of cells was seen on the surface of AHP. A significant lower compression strength and modulus were obtained in the specimens created using AHPB compared to those made with AHP and WRST (p < 0.05). The removal of calcium silicates may be quite tricky during endodontic retreatment. In conclusion, considering the limitations of the present in vitro study, both calcium silicate sealers demonstrated good physicochemical properties. However, the lower compression strength and modulus of AHPB may facilitate its removal and make the retreatment procedures considerably easier.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.