Highly uniform (111)-faceted Si sawtooth with underlying hollow structures is formed by homo-epitaxy on a U-shaped patterned Si (001) substrate. With in-situ III-V growth on such substrates by the III-V/IV dual chamber molecular beam epitaxy, a high-quality GaAs film is obtained. The (111)-faceted sawtooth structures are found effectively annihilating the antiphase boundaries and terminating mostly the lattice mismatch induced dislocations at the III-V/Si interface, while the hollow structures can effectively reduce the thermal stress. The high-quality GaAs layers on (111)-faceted hollow Si (001) are measured with a threading dislocation density of ∼106 cm−2 via the electron channeling contrast image method. By implementing the designed structure, strong room-temperature emission of InAs/GaAs and InAs/InGaAs quantum dots (QDs) at both O-band (1300 nm) and C/L-band (1550 nm) telecommunication wavelengths are achieved on Si (001) substrates. The O-band emission of InAs/GaAs QDs on Si (001) shows similar intensity to that on the GaAs substrate.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.