Solidification structures of high carbon rectangular billet with a size of 180 mm × 240 mm in different secondary cooling conditions were simulated using cellular automaton-finite element (CAFE) coupling model. The adequacy of the model was compared with the simulated and the actual macrostructures of 82B steel. Effects of the secondary cooling water intensity on solidification structures including the equiaxed grain ratio and the equiaxed grain compactness were discussed. It was shown that the equiaxed grain ratio and the equiaxed grain compactness changed in the opposite direction at different secondary cooling water intensities. Increasing the secondary cooling water intensity from 0.9 or 1.1 to 1.3 L/kg could improve the equiaxed grain compactness and decrease the equiaxed grain ratio. Besides, the industrial test was conducted to investigate the effect of different secondary cooling water intensities on the center carbon macrosegregation of 82B steel. The optimum secondary cooling water intensity was 0.9 L/kg, while the center carbon segregation degree was 1.10. The relationship between solidification structure and center carbon segregation was discussed based on the simulation results and the industrial test.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.