In this study, we fabricated polyvinyl alcohol (PVA)/chitosan (CS) bilayer films by casting and investigated the effects of preparation conditions and CS content (2, 2.5, or 3 wt.%) on the ability of these films to preserve packaged strawberries. The best performance was achieved at a CS loading of 2.5 wt.% (ultrasound time, 25 min); the strain and stress values were 143.15 ± 6.43% and 70.67 ± 0.85 MPa, respectively, oxygen permeability was 0.16 ± 0.08 cm2·m2·day−1·MPa−1, water vapor permeability was 14.93 ± 4.09 g·cm−1·s−1·Pa−1, and the shelf life of fresh strawberries packaged in the PVA/CS 2.5 wt.% bilayer film was determined to be 21 days at 5 ± 2 °C and a relative humidity of 60 ± 5%. Treatment with PVA/CS bilayer films prevented the decrease in the firmness of strawberries during storage (21 days). The evaluated physicochemical parameters (weight loss, decay, firmness, titratable acidity, soluble solid content, ascorbic acid content, and color) indicated that treatment with PVA/CS bilayer films led to better maintenance of the fruit quality. We believe that our study makes a significant contribution to literature because it paves the way to the fabrication of smart packaging materials and facilitates the commercialization of fresh strawberries as an important health food.
In this experiment, we studied the effect of poly(lactic acid)/poly(butylene adipate-co-terephthalate) (PLA/PBAT) blend films on the efficiency of passion fruit preservation at 20 °C. The weight loss, shrinkage index, firmness, and total sugar of passion fruit packaged with PLA/PBAT films had no significant differences compared with PE films during 21 days (p > 0.05). PLA/PBAT films can more effectively reduce the rising of ethanol content and delay the total acid, ascorbic acid, and sensory evaluation. Compared with unpackaged (CK) and polyethylene (PE) films, PLA/PBAT films are more conducive to preserve the overall flavor of passion fruit during storage time, in agreement with sensory evaluation, tested by E-nose, E-tongue, and GC-MS, which also proved that it can effectively maintain the edible quality of passion fruit during storage time. We believe that our study makes a significant contribution to literature because it paves the way to the generalization and application of packaging films based on composite antibacterial polymers and facilitates the commercialization of fresh passion fruit as an important health food.
The quality of blueberry fruit is easily altered after harvest. We investigated the regulatory mechanism of heat-shock (postharvest treatment) and edible coating (preharvest treatment) on the post-harvest physiological quality of blueberry from the perspective of physiological, biochemical and organoleptic characteristics. In our research, the optimal TKL concentration and the appropriate range of heat-shock temperatures were first screened based on actual application results, and then a combination of heat-shock temperature and TKL coating with significant differences in preservation effects was selected to investigate the effects of different heat-shock temperatures and TKL60 composite coating on post-harvest quality and volatile compound concentration of blueberries under refrigerated conditions. Our results showed that TKL with 60 mg/L thymol can retard the development of the degree of membrane lipid peroxidation and effectively reduce the incidence of fruit decay and the severity of blueberries infected with major pathogens at 25 °C. Meanwhile, heat-shock treatments were effective in maintaining the quality of blueberries, with a certain advantage from 45 °C to 65 °C after 8 d of storage at ambient temperature, but these treated groups were slightly inferior to TKL60 groups for fresh-keeping effect. Remarkably, the combination of heat-shock treatment and edible coating application could extend the shelf life of blueberries by 7–14 d compared to the results obtained with coating alone under low temperature storage. Specifically, heat treatment at 45 °C for 60 min after TKL60 coating (HT2) retarded the decrease in the levels of ascorbic acid, total anthocyanin, total acid and soluble solids. Gas chromatography–mass spectrometry hierarchical clustering analysis showed that this treatment also improved the aroma of the fruit, which maintained a certain similarity with that of fresh blueberries after 14 d. Principal component analysis (PCA) of the results of the evaluations carried out using an electronic nose (E-nose) and electronic tongue (E-tongue) showed that blueberries of the HT2 treated group did not show a large placement change of the PC1 distribution area from that of the fresh and blank control group. Accordingly, the combination of coating with heat-shock treatment can effectively improve the post-harvest quality and aroma compound concentration of blueberries, showing good application potential in storage and preservation of fresh fruits such as blueberries.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.