This paper reports the preparation of Kevlar-Nomex copolymer nano-composites with exfoliated pristine and functionalized graphene sheets (Grs). The graphene oxide (GrO) platelets were amidized by the reaction of amine-terminated aramid (Ar) with the functional groups present on the GrO surface to prepare the nano-composites films with different loadings of GrO. Chemical changes involved during the oxidation and subsequent amidation were monitored by Raman, FTIR and XP spectroscopic analyses. Morphology of the composite films was studied by atomic force and scanning electron microscopies. Viscoelastic properties of the hybrid films were studied for their glass transition temperature (Tg) and storage modulus by dynamical mechanical thermal analysis (DMTA). A higher shift in glass transition temperature was obtained by chemically binding the aramid copolymer chains on the functionalized Gr sheets. The increase in tensile strength and modulus at various loadings of GrO are compared with the composites using pristine Gr. The effect of interfacial interactions between the matrix chains and the reinforcement on the properties of these hybrids have been explained.
In this work in-situ polymerization technique has been used to chemically link the functionalized multiwalled carbon nanotubes (CNTs) with aramid matrix chains. Phenylene diamine monomers were reacted in the first stage with the carboxylic acid functionalized CNTs and then amidized in-situ using terephthaloyl chloride generating chemically bonded CNTs with the matrix. Various proportions of the CNTs were used to prepare the hybrid materials. The functionalization procedure was studied by Fourier transform infrared (FTIR) spectroscopy and composite morphology investigated by scanning electron microscopy (SEM). Thermal mechanical properties of these hybrids, together with those where pristine CNTs with similar loadings were used, are compared using tensile and dynamic mechanical analysis (DMA). The tensile strength and temperature involving α-relaxations on CNT loading increased with CNT loading in both systems, but much higher values, i.e., 267 MPa and 353 °C, respectively, were obtained in the chemically bonded system, which are related to the nature of the interface developed as observed in SE micrographs. The water absorption capacity of the films was significantly reduced from 6.2 to 1.45% in the presence pristine CNTs. The inclusion of pristine CNTs increased the electric conductivity of the aramid films with a minimum threshold value at the loading of 3.5 wt % of CNTs. Such mechanically strong and thermally stable aramid and easily processable composites can be suitable for various applications including high performance films, electromagnetic shielding and radar absorption.
Aramid-multiwalled carbon nanotubes (Ar-MWCNTs) nano-composites with different CNTs loadings were prepared by the solution blending technique. Aramid oligomeric chains having reactive amine end-groups were covalently grafted and wrapped over the surface of acid- CNTs reduced the stress-transfer problem in the composite material and resulted in higher modulus value of 4.26 GPa and a T g value of 338.5 o C whereas the CTE value was reduced to 101.8 ppm/C on addition of only 2.5 wt. % CNT in the aramid matrix.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.