We optimize the elaboration of very thin film of poly(vinylidene fluoride) (PVDF) polymer presenting a well-controlled thickness, roughness, and nano-inclusions amount. We focused our effort on the spin coating elaboration technique which is easy to transfer to an industrial process. We show that it is possible to obtain continuous and smooth thin films with mean thicknesses of 90 nm by properly adjusting the concentration and the viscosity of the PVDF solution as well as the spin rate and the substrate temperature of the elaboration process. The electro-active phase content versus the magnetic and structural properties of the composite films is reported and fully discussed. Last but not least, micro-patterning optical lithography combined with plasma etching has been used to obtain well-defined one-dimensional micro-stripes as well as squared-rings, demonstrating the easy-to-transfer silicon technology to polymer-based devices.

A sol-gel dip-coating process was used to deposit almost stress-free highlyc-axis oriented zinc oxide (ZnO) thin films onto glass substrates. The effects of low silver doping concentration (Ag/Zn < 1%) on the structural, morphological, optical, and waveguide properties of such films were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy, UV-Visible spectrophotometry, and M-lines spectroscopy (MLS). XRD analysis revealed that all the films were in single phase and had a hexagonal wurtzite structure. The grain size values were calculated and found to be about 24–29 nm. SEM micrographs and AFM images have shown that film morphology and surface roughness were influenced by Ag doping concentration. According to UV-Vis. measurements all the films were highly transparent with average visible transmission values ranging from 80% to 86%. It was found that the Ag contents lead to widening of the band gap. MLS measurements at 632.8 nm wavelength put into evidence that all thin film planar waveguides demonstrate a well-guided fundamental mode for both transverse electric and transverse magnetic polarized light. Moreover, the refractive index of ZnO thin films was found to increase by Ag doping levels.