The aim of the present work was to investigate the effect of physical structures on the properties of starch granules. Starches with a high amylopectin content possessing A- and B-type crystallinity were chosen for the study. The gelatinization temperature decreased in the following order: maize (A) > potato (B) > wheat (A) > barley (A), which did not reflect a correlation with the type of crystallinity. Low values of gelatinization temperature were accompanied with high free surface energy of the crystallites. It is proposed that these data are caused by different types of imperfections in starch crystals. Annealing resulted in an enhancement of the gelatinization temperature and a decrease of the free surface energy of the crystallites for all starches reflecting a partial improvement of crystalline perfection. A limited acid hydrolysis (lintnerization) of the starches decreased the gelatinization temperature because of a partial disruption of the crystalline lamellae and an increase of the amount of defects on the edges of the crystallites. Annealing of the lintnerized starches improved the structure of maize and potato starch, giving them similar structural and physicochemical parameters, which was opposite the behavior of the annealed sample from wheat. The possible nature of removable and nonremovable defects inside the crystalline region of the starch granules is discussed. It is concluded that, besides the allomorphic A- and B-types of crystal packing, physical defects in the crystals possess a major impact on starch gelatinization.

The effect of amylose deposition on the amylopectin crystalline lamellar organization in potato starch granules was studied by mild acid, so-called lintnerization, of potato tuber starch transgenically engineered to deposit different levels of amylose. The starch granules were subjected to lintnerization at different temperatures (25, 35, and 45°C) and to two levels of solubilization, ∼ 45 and 80%. The rate of the lintnerization increased with temperature but was suppressed by amylose. The molecular size of the lintner dextrins increased with temperature, but this effect was suppressed by the presence of amylose. At high temperatures and low-amylose content, the degree of branches was high with the concomitant increase in size in the dextrins. A portion of the branches was resistant to debranching enzymes possibly due to specific structural formations. The effects of temperature suggested a unique granular architecture of potato starch, and a model showing the dependence of temperature on the dynamic arrangement of amylopectin and amylose in the crystalline and amorphous lamellae for the potato starch is suggested.

Morphology, molecular structure, and thermal properties of potato starch granules with low to high phosphate content were studied as an effect of mild acid hydrolysis (lintnerization) to 80% solubilization at two temperatures (25 and 45°C). Light microscopy showed that the lintners contained apparently intact granules, which disintegrated into fragments upon dehydration. Transmission electron microscopy of rehydrated lintners revealed lacy networks of smaller subunits. The molecular composition of the lintners suggested that they largely consisted of remnants of crystalline lamellae. When lintnerization was performed at 45°C, the lintners contained more of branched dextrins compared to 25°C in both low and intermediate phosphate-containing samples. High-phosphate-containing starch was, however, unaffected by temperature and this was probably due to an altered amylopectin structure rather than the phosphate content. After lintnerization, the melting endotherms were broad with decreased onset and increased peak melting temperatures. The relative crystallinity was lower in lintners prepared at 45°C. A hypothesis that combines the kinetics of lintnerization with the molecular and thermal characteristics of the lintners is presented.

No abstract