The incorporation of hybrid fillers such as conducting polymer/graphene in polymer matrices affords promising materials with high dielectric constant suitable for electronic devices. Initially PANI/GO hybrid was prepared via in situ oxidative polymerization of aniline on GO. The hybrid was dispersed in dichlorobenzene and then incorporated in epoxy resin. The evaporation of the solvent resulted in in situ reduction of GO and the mixture was cured. The effect of PANI/rGO hybrid filler on the morphology, electrical conductivity, dielectric, dynamic mechanical, and thermal properties of epoxy nanocomposites was evaluated. The electrical conductivity of the nanocomposite containing 9 wt% of the filler (EPG9) enhanced by five orders of magnitude compared to neat epoxy, that is, from 5.6 × 10−13 to 1.27 × 10−8 S/cm. A high dielectric constant (ε′) of 208 was achieved for EPG9. The dielectric loss tangent (tan δ) was low for the hybrid nanocomposites at 103 Hz. DMA studies revealed that the storage modulus (E′) increased significantly with the incorporation of hybrid fillers. The tensile strength and Young's modulus of the EPG3 nanocomposites improved by 14.3% and 33.1%, respectively compared to neat epoxy. SEM and TEM studies revealed the uniform dispersion of the hybrid filler at 3 wt% in the epoxy matrix. The addition of PANI/rGO filler also improved the thermal stability of the epoxy nanocomposites.
Dynamically vulcanized blends of 85/15 polystyrene (PS)/natural rubber (NR) were prepared by melt mixing in an internal mixer at I70°C using dicumyl peroxide (DCP). The concentration of DCP was varied from 0 to 4.2 milliequivalents (meq). It was found that dynamic vulcanization of the blend with 2.8 meq DCP significantly enhanced the Young's modulus, flexural modulus, and impact strength, with a marginal improvement in tensile and flexural strengths. The SEM studies revealed that the morphology of the blends changed drastically on dynamic vulcanization. The dynamic mechanical studies showed that the storage modulus and the loss modulus were better for dynamically vulcanized blends with 2.8 meq DCP in comparison to other blends. The rheology studies reveal that the damping of the blend was reduced at the melt processing conditions at a DCP content of 2.8 meq and the blend was pseudoplastic in nature. The thermal stability of the dynamically vulcanized blend improved on dynamic vulcanization. Thus, dynamic vulcanization can be employed as a means of technological compatibili-zation technique for 85/15 PS/NR blend for overall improvement in properties.
In this work, polyaniline nanorod adsorbed on reduced graphene oxide (P@G) hybrid filler was prepared via in situ polymerization of aniline monomer in the presence of reduced graphene oxide as template. Fourier transform infrared, X‐ray diffraction, field emission scanning electron microscopy, and high‐resolution transmission electron microscopy images revealed the formation of P@G hybrid. The P@G hybrid was dispersed in dichlorobenzene and then introduced into epoxy resin at different loadings. The epoxy nanocomposites containing 9 wt% P@G hybrids (E/P@G9) exhibited a maximum DC conductivity of 1.34 × 10−5 S/cm that is eight orders higher compared to pure epoxy. At 103 Hz, a dielectric constant (ε′) of 163 was attained for E/P@G9, nearly 34 times higher than pure epoxy. A percolation threshold of 4 vol% was observed for ε′. Dynamic mechanical studies showed that significant enhancement in storage modulus values were exhibited for 3 and 5 wt% of hybrids. The glass transition temperature showed a maximum shift of 10°C to higher temperatures at 3 wt% loading of P@G hybrids (E/P@G3). The tensile strength, Young's modulus, and impact strength of the E/P@G3 nanocomposites enhanced by 19.7, 72, and 12%, respectively. The thermal stability of the epoxy nanocomposites also enhanced with the addition of P@G hybrid.
Cellulose nanofibers have gained much interest because of its high mechanical properties, tunable surface groups, excellent strength/weight ratio, biodegradability and low cost. The present work deals with the isolation of cellulose nanofibres from Areca spathe which is an agricultural waste. Cellulose nanofibres can be conveniently extracted from Areca spathe by sulphuric acid hydrolysis. The steps involved chemomechanical methods such as grinding, homogenization, alkali treatment, bleaching and sulphuric acid hydrolysis. After alkali treatment and bleaching, the α-cellulose content was found to increase tremendously. The removal of hemicellulose and lignin was confirmed by the FTIR studies. The increase in crystallinity was confirmed by the XRD analysis. Surface morphological studies using SEM revealed that the extracted fibres had a diameter of 55-70 nm. Thermogravimetric analysis results showed that thermal stability improved significantly for bleached fibres compared to alkali-treated, nanofibres and raw fibres.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.