Nail-head pull-through, lateral nail resistance, and single shear nailed joint tests were conducted on medium density fiberboard (MDF) with different density profiles, and the relations between the results of these tests and the density profiles of MDF were investigated. The maximum load of nail-head pull-through and the maximum load of nailed joints were little affected by the density profile. However, the ultimate strength of lateral nail resistance, the stiffness, and the yield strength of nailed joints were affected by the density profile of MDF and showed high values when the surface layer of the MDF had high density. It is known that bending performance is also influenced by density profile. Therefore, the stiffness and the yield strength of nailed joints were compared with the bending performance of MDF. The stiffness of nailed joints was positively correlated with the modulus of elasticity (MOE); in the case of CN65 nails, the initial stiffness of joints changed little in response to changes in MOE. The yield strength of nailed joints had a high positive correlation with the modulus of rupture (MOR). The stiffness and the yield strength of nailed joints showed linear relationships with MOE and MOR, respectively

No abstract

La industria de la madera requiere información sobre las características tecnológicas del material para que se les incorpore a nuevos productos con valor agregado. El objetivo de la investigación que se describe fue determinar la densidad, el módulo dinámico, el módulo de rigidez y el coeficiente de amortiguamiento de 22 especies. De cada una se prepararon 20 probetas y se realizaron pruebas de vibraciones en condiciones de apoyo libre-libre. Se calcularon el módulo de dinámico, el módulo de rigidez y el coeficiente de amortiguamiento. Para cada variable se calculó la media, desviación estándar y coeficiente de variación. La especie se consideró el factor de variación. Se obtuvieron las regresiones lineales para un nivel de significancia de 95 % y los coeficientes de determinación de las variables en función de la densidad. Cada taxon presentó características dinámicas diferentes, lo que permitió observar el amplio intervalo de valores que se pueden presentar entre diferentes taxa. La densidad se distribuyó en un intervalo amplio con un mínimo de 391 kg m-3 (Gyrocarpus americanus) y un máximo de 1 096 kg m-3 (Tabebuia chrysantha). Y se mostró como un buen predictor tanto del módulo dinámico (R2 = 0.86), como del módulo de rigidez (R2 = 0.79). No se registró una correlación significativa del coeficiente de amortiguamiento con la densidad (R2 = 0.01).

La madera laminada potencialmente puede sustituir a la madera sólida para elaborar un material de ingeniería menos variable y más homogéneo. Existe poca información que compare simultáneamente, y en una misma especie, las velocidades del ultrasonido y los módulos dinámicos en madera sólida versus laminada. El objetivo de la investigación fue verificar experimentalmente, en probetas de pequeñas dimensiones, si las características de la madera laminada de Pinus pseudostrobus son similares a las de la madera sólida. Para ello, se calcularon sus densidades y se realizaron pruebas de ultrasonido en las direcciones radial, tangencial y longitudinal. También, se determinaron las velocidades y los módulos dinámicos. Los resultados indican que la densidad de la madera laminada aumenta en comparación con la de la madera sólida. Las velocidades y los módulos dinámicos disminuyen en las direcciones radial y tangencial; en cambio, aumentan para la dirección longitudinal. Se verificó experimentalmente que las magnitudes de la densidad, la velocidad y el módulo dinámico en madera laminada son similares a las de madera sólida de esta especie. La variabilidad en las características estudiadas disminuye como efecto de reconstituir madera sólida. Para las velocidades y los módulos dinámicos de la madera sólida, sus relaciones de anisotropía muestran proporciones similares a las encontradas en la literatura, pero las magnitudes son particulares a cada especie. La investigación aporta datos de referencia y demuestra que la madera sólida y laminada, de P. pseudostrobus puede ser caracterizada con un método no destructivo.

RESUMEN Existe evidencia empírica de que la madera laminada, comparativamente con la madera sólida mejora su densidad aparente y su módulo de elasticidad. El objetivo de la investigación fue determinar la densidad, la velocidad de onda y el módulo dinámico por ondas de esfuerzo en madera sólida y laminada de Enterolobium cyclocarpum, Tabebuia rosea y Juglans pyriformis. Se elaboraron probetas de madera sólida y laminada de pequeñas dimensiones y se realizaron pruebas de ondas de esfuerzo. La densidad aparente de la madera laminada, en comparación con la de la madera sólida, se incrementa para las tres especies. En cambio, el módulo dinámico de la madera laminada aumenta para Enterolobium cyclocarpum y Tabebuia rosea, pero disminuye para Juglans pyriformis. La variabilidad de la densidad aparente, la velocidad de onda y el módulo dinámico, aumentan o disminuyen según se trate de la especie y o del parámetro en cuestión. Los resultados son válidos para el caso de laminado de pequeñas probetas de las especies estudiadas. Para su aplicación a proyectos de ingeniería, es recomendable realizar estudios ex profeso. Palabras clave: densidad aparente; velocidad de onda; módulo dinámico. Mechanical characterization by stress waves of the laminated wood of three angiosperm species ABSTRACT There is empirical evidence that laminated wood, compared to solid wood, improves its bulk density and modulus of elasticity. The objective of the research was to determine the apparent density, the wave velocity and the dynamic modulus by stress waves in solid and laminated wood of Enterolobium cyclocarpum, Tabebuia rosea and Juglans pyriformis. Solid and laminated wood specimens of small dimensions were prepared, and stress wave tests were carried out. The apparent density of laminated wood, in comparison with that of solid wood, increases for all three species. In contrast, the dynamic modulus of laminated wood increases for Enterolobium cyclocarpum and Tabebuia rosea but decreases for Juglans pyriformis. The variability of the apparent density, the wave velocity and the dynamic modulus, increases or decreases depending on the species and/or parameter in question. The results are valid for the case of laminated small specimens of the species studied. For its application to engineering projects, it is advisable to carry out ex profeso studies.

<p><strong>Objetivo: </strong>determinar el módulo dinámico por ultrasonido en especímenes de madera de <em>Enterolobium cyclocarpum</em>, <em>Tabebuia rosea</em> y <em>Juglans pyriformis</em>.<strong></strong></p><p><strong>Método: </strong>se prepararon 35 probetas de madera sólida y 35 de madera laminada, con el fin de determinar su contenido de humedad, las densidades aparentes, las velocidades del ultrasonido y los módulos dinámicos.<strong></strong></p><p><strong>Resultados: </strong>las magnitudes son diferentes entre los dos tipos de probetas. Tanto para la madera sólida como la laminada de <em>E. cyclocarpum</em>. <em>T. rosea</em> y <em>J. pyriformis</em>, las densidades aparentes se incrementan, pero las velocidades del ultrasonido disminuyen.<strong></strong></p><p><strong>Limitaciones: </strong>los resultados se circunscriben al caso de estudio para las maderas de <em>E. cyclocarpum</em>, <em>T. rosea</em> y <em>J. pyriformis</em>. Las conclusiones se refieren a las condiciones experimentales detalladas en esta investigación.</p><p><strong>Principales hallazgos: </strong>los módulos dinámicos de la madera laminada se incrementan en comparación con los parámetros de la madera sólida de <em>E. cyclocarpum</em> y <em>T. rosea</em>, pero disminuyen para <em>J. pyriformis</em>.</p>

<p><span lang="ES-MX">El objetivo de la investigación fue evaluar el efecto del densificado de la madera de <em>Gyrocarpus americanus</em> en su módulo dinámico determinado por ondas de esfuerzo. La estrategia experimental consistió en realizar pruebas de ondas de esfuerzo antes y después del tratamiento de densificado. Se determinaron la densidad de la madera, la velocidad de onda, el módulo dinámico y el coeficiente de densificado. El diseño experimental consistió en pruebas de normalidad y de diferencia de medias para la densidad, velocidad de onda y módulo dinámico para antes y después densificado. Se calcularon regresiones lineales y coeficientes de determinación para la velocidad de onda y el módulo dinámico, en función de la densidad. Los principales resultados fueron: la magnitud del coeficiente de densificado fue comparable a la reportada en la bibliografía; la velocidad de onda no varió significativamente antes y después del densificado; el densificado incrementó la densidad y el módulo dinámico de la madera de <em>G. americanus.</em></span></p>

El objetivo de la investigación fue determinar los coeficientes de higroexpansión, de higrocontracción y sus relaciones de anisotropía de ocho maderas mexicanas: Cupressus lindleyi, Cedrela odorata, Swietenia macrophylla, Tabebuia donnell-smithii, Fraxinus uhdei, Fagus mexicana, Dalbergia palo-escrito y Guazuma ulmifolia. Se realizaron pruebas de higroscopía con un procedimiento de humidificación y secado de probetas de pequeñas dimensiones. Las magnitudes de las higroexpansiones e higrocontracciones son similares a las de otras especies mexicanas reportadas en la literatura. Los coeficientes denotan un carácter anisotrópico en las direcciones radial y tangencial. La densidad de la madera es un buen predictor de los coeficientes. Sin embargo, las correlaciones de las relaciones de anisotropía son diferentes a las reportadas en trabajos anteriores. DOI: https://doi.org/10.54167/tecnociencia.v16i1.869