In order to improve the contribution to sustainability of cement production, several strategies have been developed, such as the incorporation of additions as clinker replacement. Regarding the production of commercial cements with additions, those made with binary binders are mostly produced. However, the use of ternary binders for manufacturing commercial cements is still very low, at least in Spain, and they could also be an adequate solution for producing eco-friendly cements. The objective of this research is to study the effects in the long term produced by ternary binders which combine the additions of blast furnace slag, fly ash and limestone in the microstructure, durability and mechanical performance of mortars, compared to mortars without additions and mortars made with binary binders. The ternary and binary binders accomplished the prescriptions for a cement type CEM II/B. The microstructure was characterized using mercury intrusion porosimetry, electrical resistivity and differential thermal analysis. Absorption after immersion, diffusion coefficient, mechanical strengths and ultrasonic pulse velocity were studied. The best performance was noted for ternary binder with both slag and fly ash, probably produced by the synergetic effects of slag hydration and fly ash pozzolanic reactions. These effects were more noticeable regarding the compressive strength.
The use of eco-friendly cements prepared with ternary binders could contribute to improving the sustainability of cement production. However, their use for manufacturing commercial cements is very low, at least in Spain. The purpose of this research is to study the behavior in the long term of mortars made with ternary binders which incorporated ground granulated blast furnace slag, fly ash, and limestone, exposed to environmental conditions compatible with the specifications of exposure class XC3 of the Eurocode 2, compared to mortars without additions and mortars with binary binders. The exposure station was placed in an underground floor of a building used as a garage with circulation of vehicles and moderately high CO2 concentration. The ternary and binary binders verified the prescriptions of cement type CEM II/B. The microstructure was characterized using mercury intrusion porosimetry and electrical resistivity. Water absorption, diffusion coefficient, carbonation depth, mechanical strengths, and ultrasonic pulse velocity were determined. A loss of microstructure refinement with time was noted for all the analyzed binders, probably related to the development of carbonation and drying shrinkage. The binary mortars with slag and fly ash and the ternary binder which combined them showed the best mechanical performance at 250 days.
For improving the contribution of the cement industry to mitigate global warming, many strategies have been put into practice, such as the use of eco-friendly cements with the incorporation of additions substituting clinker. Nevertheless, the use of ternary binders for the production of commercial cements is still reduced, particularly in Spain. The purpose of this research is to characterize the long-term influence produced by the exposure to a real in situ inland Mediterranean climate condition in the pore network, parameters related to durability and mechanical performance of mortars made with ternary binders, which incorporated limestone, fly ash, and ground granulated blast-furnace slag, in comparison with mortars without additions and binary blended mortars. The site verified the specifications of exposure class XC4 of Eurocode 2. The ternary and binary binders accomplished the prescriptions of cement type CEM II/B. The pore network was studied with mercury intrusion porosimetry and electrical resistivity. Water absorption, diffusion coefficient, carbonation depth, ultrasonic pulse velocity, compressive and flexural strengths have been determined. The exposure to the environment produced after 250 days an increase in porosity, a loss of pore refinement, a rise of the carbonation depths, and a reduction in the mechanical strengths, highlighting the better overall performance of ternary mortar with both fly ash and slag.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.