Novel polyurethane co-polymers (TPUs), based on poly(ϵ-caprolactone)-block-poly(dimethylsiloxane)-block-poly(ϵ-caprolactone) (PCL-PDMS-PCL) as soft segment and 4,4'-methylenediphenyl diisocyanate (MDI) and 1,4-butanediol (BD) as hard segment, were synthesized and evaluated for biomedical applications. The content of hard segments (HS) in the polymer chains was varied from 9 to 63 wt%. The influence of the content and length of the HS on the thermal, surface, mechanical properties and biocompatibility was investigated. The structure, composition and HS length were examined using (1)H- and quantitative (13)C-NMR spectroscopy. DSC results implied that the synthesized TPUs were semicrystalline polymers in which both the hard MDI/BD and soft PCL-PDMS-PCL segments participated. It was found that an increase in the average HS length (from 1.2 to 14.4 MDI/BD units) was accompanied by an increase in the crystallinity of the hard segments, storage moduli, hydrophilicity and degree of microphase separation of the co-polymers. Depending on the HS content, a gradual variation in surface properties of co-polymers was revealed by FT-IR, AFM and static water contact angle measurements. The in vitro biocompatibility of co-polymers was evaluated using the endothelial EA.hy926 cell line and protein adsorption on the polyurethane films. All synthesized TPUs adsorbed more albumin than fibrinogen from multicomponent protein mixture, which may indicate biocompatibility. The polyurethane films with high HS content and/or high roughness coefficient exhibit good surface properties and biocompatible behavior, which was confirmed by non-toxic effects to cells and good cell adhesion. Therefore, the non-cytotoxic chemistry of the co-polymers makes them good candidates for further development as biomedical implants.
Novel polyurethane copolymers derived from 4,4 0 -methylenediphenyl diisocyanate (MDI), 1,4-butanediol (BD) and a,x-dihydroxy-[poly(caprolactone)-polywere synthesized by a two-step polyaddition reaction in solution. In the synthesis of the polyurethanes, the PCL blocks served as a compatibilizer between the nonpolar PDMS blocks and the polar comonomers, MDI and BD. The synthesis of thermoplastic polyurethanes (TPU) with high soft segment contents was optimized in terms of the concentrations of the reactants, the molar ratio of the NCO/OH groups, and the time and temperature of the polyaddition reaction. The structure, composition, and hard MDI/BD segment length of the synthesized polyurethane copolymers were determined by 1 H, 13 C-NMR, and two-dimensional correlation (COSY, HSQC, and HMBC) spectroscopy, while the hydrogen bonding interactions in the copolymers were analyzed by FT-IR spectroscopy. The influence of the reaction conditions on the structure, molecular weight, thermal, and some physical properties was studied at constant composition of the reaction mixture. A change in the molar ratio of the NCO/OH groups and the reaction conditions modified not only the molecular weight of the synthesized polyurethanes, but also the microstructure and therefore the thermal and physical properties of the copolymers. It was demonstrated that only PCL segments with high soft segment contents crystallize, thereby showing spherulitic morphology.
A series of novel thermoplastic elastomers, based on poly(dimethylsiloxane) (PDMS) as the soft segment and poly(butylene terephthalate) (PBT) as the hard segment, were synthesized by catalyzed two‐step, melt transesterification reactions of dimethyl terephthalate and methyl esters of carboxypropyl‐terminated poly(dimethylsiloxane)s (M̄n = 550–2170 g mol−1) with 1,4‐butanediol. The lengths of both the hard and soft segments were varied while the weight ratio of the hard to soft segments in the reaction mixture was maintained constant (57/43). The molecular structure, composition and molecular weights of the poly(ester–siloxane)s were examined by 1H NMR spectroscopy. The effectiveness of the incorporation of the methyl‐ester‐terminated poly(dimethylsiloxane)s into the copolymer chains was verified by chloroform extraction. The effect of the segment length on the transition temperatures (Tm and Tg) and the thermal and thermo‐oxidative degradation stability, as well as the degree of crystallinity and hardness properties of the synthesized TPESs, were studied. Copyright © 2003 Society of Chemical Industry
Properties and biocompatibility of a series of thermoplastic poly(urethane-siloxane)s (TPUSs) based on α,ω-dihydroxy ethoxy propyl poly(dimethylsiloxane) (PDMS) for potential biomedical application were studied. Thin films of TPUSs with a different PDMS soft segment content were characterized by (1) H NMR, quantitative (13) C NMR, Fourier transform infrared spectroscopy (FTIR), atomic force microscopy (AFM), differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), contact angle, and water absorption measurements. Different techniques (FTIR, AFM, and DMA) showed that decrease of PDMS content promotes microphase separation in TPUSs. Samples with a higher PDMS content have more hydrophobic surface and better waterproof performances, but lower degree of crystallinity. Biocompatibility of TPUSs was examined after attachment of endothelial cells to the untreated copolymer surface or surface pretreated with multicomponent protein mixture, and by using competitive protein adsorption assay. TPUSs did not exhibit any cytotoxicity toward endothelial cells, as measured by lactate dehydrogenase and 3-[4,5-dimethylthiazol-2-yl]-2,5-diphenyl-tetrazolium bromide assays. The untreated and proteins preadsorbed TPUS samples favored endothelial cells adhesion and growth, indicating good biocompatibility. All TPUSs adsorbed more albumin than fibrinogen in competitive protein adsorption experiment, which is feature regarded as beneficial for biocompatibility. The results indicate that TPUSs have good surface, thermo-mechanical, and biocompatible properties, which can be tailored for biomedical application requirements by adequate selection of the soft/hard segments ratio of the copolymers.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.