The corrosion and leaching behaviour of a new ternary Sn-0.7Cu-0.05Ni alloy in 3.5 wt.% NaCl solution is reported herein. Potentiodynamic polarization measurements show that Sn-0.7Cu-0.05Ni has the highest corrosion rate. Results of the 30-day Sn leaching measurement show that Sn-Cu-Ni joint has slight decrease attributed to the formation of thin passivation film after 15 days. The leaching amounts of Sn are observed to be higher in solder joint than in solder alloy due to the galvanic corrosion happening on the surface. EDS and XRD results of the corroded surface confirm that the corroded product is made up of oxides of tin.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.