In construction industry, laminated glass is more and more used for transparent loadbearing building components. It is known that the residual load-carrying capacity after glass breakage of glass/PVB (polyvinyl butyral) laminates is relatively poor, mainly due to the limited stiffness and strength of PVB. For that reason, the failure behaviour of laminates composed with a stiffer and stronger interlayer material, called SentryGlas ® Plus (SGP), was investigated experimentally. Consequently, 1100 mm long test samples composed of two annealed float glass layers and one SGP interlayer were subjected to destructive in-plane four-points bending tests. Subsequently, different stages were distinguished during the failure process, corresponding to a different number of broken glass layers. In spite of the relatively good interlayer material properties and in contradiction to what was expected, the observed post-failure safety was poor.However, the failure mechanisms observed were significantly different from those of glass/PVB beams: due to a lack of local delamination near the glass fracture zone, tear of the SGP interlayer occurred without preceding large visual interlayer elongations.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.