Direct writing utilizing a focused electron beam constitutes an interesting alternative to resist-based techniques, as it allows for precise and flexible growth onto any conductive substrate in a single-step process. One important challenge, however, is the identification of appropriate precursors which allow for deposition of the material of choice, e.g., for envisaged applications in nano-optics. In this regard the coinage metal silver is of particular interest since it shows a relatively high plasma frequency and, thus, excellent plasmonic properties in the visible range. By utilizing the precursor compound AgOMeBu, direct writing of silver-based nanostructures via local electron beam induced deposition could be realized for the first time. Interestingly, the silver deposition was strongly dependent on electron dose; at low doses of 30 nC/μm a dominant formation of pure silver crystals was observed, while at higher electron doses around 10 nC/μm large carbon contents were measured. A scheme for the enhanced silver deposition under low electron fluxes by an electronic activation of precursor dissociation below thermal CVD temperature is proposed and validated using material characterization techniques. Finally, the knowledge gained was employed to fabricate well-defined two-dimensional deposits with maximized silver content approaching 75 at. %, which was achieved by proper adjustment of the deposition parameters. The corresponding deposits consist of plasmonically active silver crystallites and demonstrate a pronounced Raman signal enhancement of the carbonaceous matrix.

No abstract

Focused electron beam induced deposition (FEBID) is a flexible direct-write method to obtain defined structures with a high lateral resolution. In order to use this technique in application fields such as plasmonics, suitable precursors which allow the deposition of desired materials have to be identified. Well known for its plasmonic properties, silver represents an interesting candidate for FEBID. For this purpose the carboxylate complex silver(I) pentafluoropropionate (AgO2CC2F5) was used for the first time in FEBID and resulted in deposits with high silver content of up to 76 atom %. As verified by TEM investigations, the deposited material is composed of pure silver crystallites in a carbon matrix. It showed good electrical properties and a strong Raman signal enhancement. Interestingly, silver crystal growth presents a strong dependency on electron dose and precursor refreshment.