Tree bark is a by-product of the timber industry available in large amounts, considering that approximately 10% of the volume of a tree stem is bark. Bark is used primarily for low-value applications such as heat generation or as mulch. To the best of our knowledge, this study is the first one that scrutinises thermal insulation panels made from spruce bark fibres with different densities and fibre lengths manufactured in a wet process. The insulation boards with densities between 160 and 300 kg/m3 were self-bonded. Internal bond, thermal conductivity, and dimensional stability (thickness swelling and water absorption), together with formaldehyde content, were analysed. The thermal properties of the boards were directly correlated with the density and reached about 0.044 W/m*K, while the internal bond was rather influenced by the fibre length and was relatively low (on average 0.07 N/mm2). The water absorption was high (from 55% to 380%), while the thickness swelling remained moderate (up to 23%). The results of this study have shown that widely available bark residues can be successfully utilised as an innovative raw material for efficient eco-friendly thermal insulation products.

Planer shavings (PS) are side-products generated during the processing of solid wood, typically used for heating, packaging, or insulation purposes. PS has been used for decades in particleboard manufacture, particularly in the core layer. The aim of this research is to investigate the use of PS with a length over 4 mm in low-density one-layer particleboard manufacturing with a thickness of 10 mm, as an option to reduce the raw material demand for wood-based panels. Correlations towards the mechanical properties of the particleboards, fabricated at a density of 475 kg/m3, could be drawn by analyzing the effects of different urea-formaldehyde adhesive contents (6%, 9%, and 12%). Two methods of adhesive application (pouring and spraying) and two types of blending of PS with adhesive (plowshare mixer and drum mixer) were investigated, with the aim that PS will have controlled resin application. The difference between the adhesive application methods was examined by analyzing the mechanical properties as an internal bond, modulus of rupture, and modulus of elasticity as well as indirectly by visualizing the adhesive distribution by adding a green pigment to the adhesive before application. PS demonstrated reduced bending properties in comparison with the EN 312 standard requirements of particleboards for internal use in dry conditions (type P2), due to the low density. The internal bond strength in the case of the particleboard without pigment application (up to 0.5 N/mm2) was higher compared to the P2 requirements (0.4 N/mm2), and significantly lower (0.15 N/mm2) in combination with the pigment (2.5% based on the board weight, compared to 0.1%, specific for such industry applications), but still superior to the values of the reference panel manufactured with wood particles.