The purpose of this work is to evaluate the performance of Ni 0.5 Zn 0.5 Fe 2 O 4 ferrite doped with 0.1 and 0.4 mol of Cu as a catalyst for the transesterification of soybean oil to biodiesel, using methanol. The samples were characterized by X-ray diffraction, nitrogen adsorption and scanning electron microscopy. The reaction was performed for 2 hours at a temperature of 160 °C, using 10 g of soybean oil, a molar ratio of oil: alcohol of 1:20, and 4% (w/w) of catalyst. The product of the reaction was characterized by gas chromatography, which confirmed conversion to methyl esters. The diffraction patterns showed the presence only of Ni 0.5 Zn 0.5 Fe 2 O 4 ferrite phase with a crystallite size of 29 nm. The samples doped with 0.1 and 0.4 mol of Cu showed a surface area and particle size of 22.17 m 2 g -1 and 50.47 nm; and 23.49 m 2 g -1 and 47.64 nm, respectively. The morphology of both samples consisted of brittle block-shaped agglomerates with a wide particle size distribution. A comparative analysis of the two catalysts indicated that the catalyst doped with 0.4 mol of Cu showed the better performance, with a conversion rate of 50.25%, while the catalyst doped with 0.1 mol of Cu showed 42.71% conversion.
The development of efficient electrocatalysts for the oxygen evolution reaction (OER) is of paramount importance in sustainable water-splitting technology for hydrogen production. In this context, this work reports mixed-valence oxide samples of the MnXCo3-XO4 type (0 ≤ X ≤ 1) synthesized for the first time by the proteic sol-gel method using Agar-Agar as a polymerizing agent. The powders were calcined at 1173 K, characterized by FESEM, XRD, RAMAN, UV–Vis, FT-IR, VSM, and XPS analyses, and were investigated as electrocatalysts for the oxygen evolution reaction (OER). Through XRD analysis, it was observed that the pure cubic phase was obtained for all samples. The presence of Co3+, Co2+, Mn2+, Mn3+, and Mn4+ was confirmed by X-ray spectroscopy (XPS). Regarding the magnetic measurements, a paramagnetic behavior at 300 K was observed for all samples. As far as OER is concerned, it was investigated in an alkaline medium, where the best overpotential of 299 mV vs. RHE was observed for the sample (MnCo2O4), which is a lower value than those of noble metal electrocatalysts in the literature, together with a Tafel slope of 52 mV dec−1, and excellent electrochemical stability for 15 h. Therefore, the green synthesis method presented in this work showed great potential for obtaining electrocatalysts used in the oxygen evolution reaction for water splitting.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.