Metal mesh: a design that revolutionizes the transparent conducting electrode (TCE) industry and drives the development of flexible optoelectronic technology.
Highly efficient and bendable organic solar cells (OSCs) are fabricated using solution‐processed silver nanowire (Ag NW) electrodes. The Ag NW films were highly transparent (diffusive transmittance ≈ 95% at a wavelength of 550 nm), highly conductive (sheet resistance ≈ 10 Ω sq−1), and highly flexible (change in resistance ≈ 1.1 ± 1% at a bending radius of ≈200 μm). Power conversion efficiencies of ≈5.80 and 5.02% were obtained for devices fabricated on Ag NWs/glass and Ag NWs/poly(ethylene terephthalate) (PET), respectively. Moreover, the bendable devices fabricated using the Ag NWs/PET films decrease slightly in their efficiency (to ≈96% of the initial value) even after the devices had been bent 1000 times with a radius of ≈1.5 mm.
An effective method for depositing highly transparent and conductive ultrathin silver (Ag) electrodes using minimal oxidation is reported. The minimal oxidation of Ag layers significantly improves the intrinsic optical and structural properties of Ag without any degradation of its electrical conductivity. Oxygen‐doped Ag (AgOx) layers of thicknesses as low as 6 nm exhibit completely 2D and continuous morphologies on ZnO films, smaller optical reflections and absorbances, and smaller sheet resistances compared with those of discontinuous and granular‐type Ag layers of the same thickness. A ZnO/AgOx/ZnO (ZAOZ) electrode using an AgOx (O/Ag = 3.4 at%) layer deposited on polyethylene terephthalate substrates at room temperature shows an average transmittance of 91%, with a maximum transmittance of 95%, over spectral range 400−1000 nm and a sheet resistance of 20 Ω sq−1. The average transmittance value is increased by about 18% on replacing a conventional ZnO/Ag/ZnO (ZAZ) electrode with the ZAOZ electrode. The ZAOZ electrode is a promising bottom transparent conducting electrode for highly flexible inverted organic solar cells (IOSCs), and it achieves a power conversion efficiency (PCE) of 6.34%, whereas an IOSC using the ZAZ electrode exhibits a much lower PCE of 5.65%.
Extensive experimental and theoretical study suggests that interchromophore electrostatic interactions are among the most severe impediments to the induction and stability of large electro-optic coefficients in electric-field-poled organic materials. In this report, multichromophore-containing dendritic materials have been investigated as a means to minimize unwanted attenuation of nonlinear optical (electro-optic) activity at high chromophore loading. The dendritic molecular architectures employed were designed to provide optimized molecular scaffolding for electric-field-induced molecular reorientation. Design parameters were based upon past experimental results in conjunction with statistical and quantum mechanical modeling. The electro-optic behavior of these materials was evaluated through experimental and theoretical analysis. Experimental data collected from the dendrimer structures depict a reasonably linear relationship between chromophore number density (N) and electro-optic activity (r(33)) demonstrating a deviation from the dipolar frustration that typically limits r(33) in conventional chromophore/polymer composite materials. The observed linear dependence holds at higher chromophore densities than those that have been found to be practical in systems of organic NLO chromophores dispersed in polymer hosts. Theoretical analysis of these results using Monte Carlo modeling reproduces the experimentally observed trends confirming linear dependence of electro-optic activity on N in the dendrimer materials. These results provide new insight into the ordering behavior of EO dendrimers and demonstrate that the frequently observed asymptotic dependence of electro-optic activity on chromophore number density may be overcome through rational design.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.