This work reports the incorporation of mixed-metal oxides (MMOs) such as Si/Ti and Si/Zr into latex paints in the form of thin coatings for permanent trapping of indoor formaldehyde. The formaldehyde removal performance of the surface coatings was evaluated in a lab-scale indoor air chamber, and the results were compared with those of powder analogues. Due to the pore blockage by the latex, the incorporation led to 6−30% reduction in adsorption capacity and 50−70% drop in the adsorption rate for MMO-latex paints relative to their powder MMO analogues. Under the operating conditions of concentration, temperature, and relative humidity, the Si/Zr-latex paints outperformed the Si/Ti counterparts. It was also observed that performance could decrease over excessive loading, for example, Si/Zr-latex paint with 15/1 Si/Zr weight ratio showed a 20% lower adsorption capacity than that of the Si/ Zr-latex paint with 25/1 Si/Zr ratio at 5 ppm v , 25 °C, and 70% RH. While high temperature greatly reduced the adsorption rate of the MMO-latex paints, high humidity slightly promoted the rate of formaldehyde capture. In 10 L, flow-through chamber tests, 25Si/Zr-latex paint reduced 5 ppm v formaldehyde by up to 60% at 25 °C and 70% RH with an adsorption rate of 0.34 ppm v /h. Overall, this study highlights the potential of MMO-latex paints with optimized formation for the efficient abatement of indoor aldehydes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.