Many low alloy steels are compositionally heterogeneous due to the preferential segregation of alloying elements to the dendritic or interdendritic regions when the steel is first solidified (microsegregation). This segregation is often ignored when using CCT diagrams to predict the phase transformation behaviour of steels, but may be of importance in some industrially-relevant cases. This work focuses on the martensite start temperature (Ms
) of Super CMV, a high strength aerospace steel, after rapid austenitisation treatment to various peak temperatures from 900 °C to 1300 °C. It was found that the average Ms
temperature increased with increasing peak temperature (and prior austenite grain size) at peak temperatures of 1100°C and above, which is to be expected conventionally. However, at peak temperatures of below 1100°C, the Ms
temperature increased with decreasing prior-austenite grain size. It is proposed that this was due to the presence of non-dissolved carbides in these conditions, particularly in enriched bands of material, which deplete the matrix and hence raise Ms
.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.