In this work, the reaction mechanism used in the preparation of fluorine-free superconducting YBa(2)Cu(3)O(7-delta) (YBCO) was investigated. To determine which precursor interactions are dominant, a comprehensive thermal analysis (thermogravimetric analysis-differential thermal analysis) study was performed. The results suggest that a three step reaction mechanism, with a predominant role for BaCO(3), is responsible for the conversion of the initial state to the superconducting phase. In the presence of CuO, the decarboxylation of BaCO(3) is kinetically favored with the formation of BaCuO(2) as a result. BaCuO(2) reacts with the remaining CuO to form a liquid which ultimately reacts with Y(2)O(3) in a last step to form YBCO. High temperature X-ray diffraction experiments confirm that these results are applicable for thin film synthesis prepared from an aqueous fluorine-free sol-gel precursor.
In this work a fluorine-free sol–gel method based on low-cost materials and water as
primary solvent is developed, resulting in a sustainable superconducting film. Using a 0.6 M
‘AWAT’ precursor (M-acetates, water, acetic acid and tri-ethanolamine, patent pending)
YBa2Cu3O7−δ (YBCO) films
were dip coated on SrTiO3
(STO) single-crystal substrates. After gelation at
60 °C, the
amorphous gel was transformed to the desired crystalline superconducting phase. Sintering was conducted
at 815 °C
under a 200 ppm oxygen partial pressure, followed by a pure oxygen annealing at
400 °C. Highly
textured (Δω = 0.2°,
Δφ = 6.5°) YBCO
films with a Tc,onset
of 92 K, a ΔTc
of 5 K, a Jc
of 0.55 MA cm−2
and an Ic
of 25 A cm−1
width at 77.3 K and self-field were achieved. Experimental results on film synthesis,
morphology, microstructure and superconducting properties are presented.
The achievement of low-cost deposition techniques for high critical current (RE)Ba 2 Cu 3 O 7−y -coated conductors is one of the major objectives in achieving a widespread use of superconductivity in power applications. Chemical solution deposition techniques are appearing as a very promising methodology to achieve highly textured oxide thin films at a low cost, so an intense effort is being carried out to develop routes for all chemically coated conductor tapes. In this work recent achievements will be presented towards the goal of the development of an environmentally friendly, completely water-based sol-gel technique for the deposition of thin superconducting films on SrTiO 3 single-crystal substrates using the dip coat technique. A comparison is made between aqueous sol-gel synthesis of two (RE)Ba 2 Cu 3 O 7−y superconducting systems: YBa 2 Cu 3 O 7−y and its homologue NdBa 2 Cu 3 O 7−y . Our conclusions are that YBa 2 Cu 3 O 7−y still remains the material of choice for coated conductor development using this sol-gel technique, with a T c,onset of 91 K and J c of 0.3 MA cm −2 .
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.