The purpose of this study was to evaluate the electrochemical corrosion resistance of the extruded magnesium alloy AZ80 in NaCl solutions. The resistance to electrochemical corrosion was evaluated on the grounds of registered anodic polarisation curves. Potentiodynamic tests were performed in solution with a concentration of 0.01-2.00 M NaCl. In addition, immersion tests were performed, and they allowed us to determine the corrosion rate. Scanning electron microscopy was applied to observe the microstructure after the immersion tests (after removing the corrosion products). Phenomena that happen on the surface of the alloy were evaluated with the application of electrochemical impedance spectroscopy. The tests enabled us to determine the impedance spectra of the system and the data obtained during the measurement was matched to the equivalent system. An optical profilometer was used for the measurement of the geometrical features of the surface of the alloy. The results of the performed tests prove explicitly the deterioration of the corrosion characteristics of the alloy with an increase in the molar concentration of the NaCl solution. A decrease of the corrosion potential and the polarisation resistance was observed, as well as an increase of the corrosion current density. It was proved that irrespective of the concentration, pitting corrosion can be found on the surface of the alloy. The potential to use the extruded magnesium alloy AZ80 in the aircraft and automotive industries is connected with the necessity to apply protective layers on elements made from the tested alloy. Keywords: extruded magnesium alloy AZ80, electrochemical corrosion, potentiodynamic and immersion tests, SEM, EIS Namen te {tudije je bil oceniti odpornost ekstrudirane magnezijeve zlitine AZ80 proti elektrokemijski koroziji v raztopini NaCl. Odpornost proti elektrokemijski koroziji je bila ugotovljena na podlagi anodnih polarizacijskih krivulj. Izvr{eni so bili potenciodinamski preizkusi v raztopini s koncentracijo od 0,01-2 M NaCl. Dodatno so bili izvr{eni tudi preizkusi s potapljanjem, ki so omogo~ili dolo~itev hitrosti korozije. Vrsti~na elektronska mikroskopija je bila uporabljena za slikanje mikrostrukture po potapljanju (po odstranitvi korozijskih produktov). Pojavi na povr{ini zlitine so bili ocenjeni z elektrokemijsko impedan~no spektroskopijo. Preizkusi so omogo~ili dolo~itev impedan~nega spektra sistema in z meritvami dobljeni podatki so se ujemali z ekvivalentnim sistemom. Opti~ni profilometer je bil uporabljen za merjenje geometrijskih pojavov na povr{ini zlitine. Rezultati izvr{enih preizkusov so potrdili poslab{anje korozijskih lastnosti zlitine pri pove~anju molske koncentracije raztopine NaCl. Opa`eno je bilo zmanj{anje korozijskega potenciala in polarizacijske odpornosti, kot tudi pove~anje gostote korozijskega toka. Dokazano je, da se ne glede na koncentracijo jami~asta korozija pojavi na povr{ini zlitine. Mo`nosti uporabe ekstrudirane magnezijeve zlitine AZ80 v letalstvu in avtomobilski industriji je povezana z nujnos...
The study presents evaluation of the influence of strain in drawing process and of surface modification on resistance to electrochemical corrosion of wires made of stainless steel for production of guide wires used in invasive cardiology. The results of static tensile test enabled us to determine the course of flow curve of wires made of X10CrNi 18-8 steel as well as mathematical form of flow stress function. Resistance to electrochemical corrosion was evaluated on the ground of registered anodic polarisation curves by means of potentiodynamic method. The tests were performed in solution simulating human blood on samples that were electrolytically polished and samples that were polished and then chemically passivated. Exemplary anodic polarisation curves were given. It was proved that with the applied strain, corrosion properties decrease. It was found that chemical passivation improves wire corrosion characteristics. Statistical analysis showed that there is a significant dependence between corrosion properties (polarisation resistanceRp) and strainεapplied in drawing process. Functions that present the changeRp=f(ε)were selected. The issue is of importance to guide wire manufacturers because application of the suggested methodology will enable us to forecast corrosion characteristics of wire with the required strength drawn with the applied strain.
The main purpose of this study was to evaluate physicochemical and electrochemical properties of AISI 316L stainless steel with modified surface, used for implants in human urinary system. In order to simulate conditions, which occur in the tissue environment of the urinary system, the test pieces were exposed in a urinary solution at temperature of T=37±1• C, for a period of 30 days. Evaluation of physicochemical properties of biomaterial was made on the basis of surface chemical analysis (XPS). To evaluate the effects which occur on the surface of the examined steel, Electrochemical Impedance Spectroscopy (EIS) method was also employed. Analysis of test results shows favourable influence of the suggested surface treatment of AISI 316L stainless steel. Samples having electrolytically polished and chemically passivated surface featured the best physicochemical and electrochemical characteristics.Keywords: AISI 316L stainless steel; electrochemical impedance spectroscopy (EIS), X-ray Photoelectron Spectroscopy (XPS), Scanning Electron Microscopy (SEM) Podstawowym kryterium przydatności biomateriału metalowego na implanty urologiczne (stenty urologiczne) jest biokompatybilność. Jest ona w głównej mierze związana z własnościami fizykochemicznymi powierzchni implantu, które powinny być dostosowane do cech środowiska tkanek układu moczowego człowieka. W celu poprawy biokompatybilności stali Cr-Ni-Mo ustalono warunki wytwarzania warstw pasywnych na jej powierzchni. Wytworzenie warstwy pasywnej obejmowało etap polerowania elektrolitycznego i pasywowania. Taki sposób obróbki powierzchniowej zapewnił chropowatość R a < 0,16 µm wymaganą dla tego rodzaju implantów. W pracy tej szczególną uwagę skoncentrowano na analizie długotrwałego oddziaływania środowiska sztucznego moczu na własności fizykochemiczne wytypowanej stali.Zasadniczym celem pracy była ocena własnościfizykochemicznych i elektrochemicznych stali AISI 316L o modyfikowanej powierzchni stosowanej na implanty w układzie moczowym człowieka. W celu zasymulowania warunków występujących w środowisku tkankowym układu moczowego próbki poddawano ekspozycji w roztworze sztucznego moczu o temperaturze T=37±1• C przez okres 30 dni. O przydatności zaproponowanej warstwy pasywnej do uszlachetniania powierzchni stali w znacznym stopniu decyduje jej skład chemiczny. Dlatego w pracy wykonano badania składu chemicznego metodą spektroskopii fotoelektronów (XPS), z użyciem wielofunkcyjnego spektrometru elektronów PHI 5700/660 firmy Physical Electronics, podczas których zidentyfikowano i wyznaczono stężenia atomowe pierwiastków w badanych warstwach pasywnych. Dla próbek przeprowadzono pomiar widma fotoelektronów w szerokim zakresie energii wiązania od 0÷1400 eV oraz dokładne pomiary linii widmowych poszczególnych pierwiastków składowych z warstwy powierzchniowej. Dla oceny zjawisk zachodzących na powierzchni badanej stali zastosowano również metodę elektrochemicznej spektroskopii impedancyjnej (EIS). Pomiary przeprowadzono z wykorzystaniem systemu pomiarowego AutoLab PGSTAT 302N wyp...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.