A BN interphase has been deposited, by isothermal/isobaric chemical vapor infiltration (ICVI) from BF3-NH3, within a preform made from ex-polycarbosilane (ex-PCS) fibers, at about 1000°C. In a second step, the BN-treated preform was densified with Sic deposited from CH3SiCI3-H2 at about the same temperature. From a thermodynamic standpoint, ex-PCS fibers could be regarded as unreactive vs the BF3-NH3 gas phase assuming they are coated with a thin layer of carbon or/and silica. The as-deposited interphase consists of turbostratic BN (N/B < 1) containing oxygen. The Sic infiltration acts as an annealing treatment: (i) the BN interphase becomes almost stoichiometric and free of oxygen; (ii) the fibers undergo a decomposition process yielding a Si02/C layer at the BN/fiber interface. The weaker link in the interfacial sequence seems to be the BN/Si02 interface. Deflection of microcracks arising from the failure of the matrix takes place at (or nearby) that particular interface. [
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.