The in-plane anisotropy (IPA) of mechanical properties existed in plate products is often undesired since it limits the industrial application and increases the difficulty of material processing. It is thus one of the important factors which requires strict control during the manufacture of highperformance aluminum alloy plates. The anisotropic behavior of TiB 2 /2024Al composite rolling sheet under different heat treatment is studied in this article. T4 heat treated specimen shows good isotropy of yield strength and its texture components are significantly weakened compared with traditional Al alloys. The evolution of microstructures for T4 specimen was studied. The submicron TiB 2 particles increase the driving force of recrystallization during rolling process and static recrystallization (SRX) is stimulated, thus induces texture randomization. Anisotropic behavior of yield strength occurs in specimen after T3 heat treatment. It is supposed that the difference in the activation of slip system under different loading direction gives rise to this anisotropy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.