Metal hollow sphere foams are fabricated by bonding millimeter sized metal alloy hollow spheres at points of contact. The spheres are formed as powder shells from slurries. For stainless steel spheres, the starting powder is a mixture of iron and chromium oxide. Thermal treatment in hydrogen reduces the oxides to Fe/Cr alloys with less than 2% porosity in sphere walls. The nominal composition is close to that of 405 stainless. Carburization in CO/CO2 atmosphere followed by heat treatment produces foams of either 410 or 420 type stainless steels depending on carbon content. Compressive stress-strain behavior was measured on point contact bonded stainless foams both before and after carburization. Hardness measurements on steel sphere walls were used to estimate the yield strength. Relative strengths of the foams were positioned between open and closed cell models. This was encouraging because bonding in the foams was less than optimum and the hollow sphere walls contained defects. As processing improves, strengths should increase. To produce titanium alloy spheres, the starting powder is titanium alloy hydride. Thermal treatment in an inert atmosphere decomposes the hydride and sinters the titanium powder in the sphere walls to greater than 96% relative density. Both titanium and Ti-6V-4V spheres and foams have been produced. Oxygen contents are a concern for titanium compositions and processing is being altered to reduce oxygen levels to increase ductility
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.