Sintered compacts of nanophase ZnO (∼60 nm average grain size, presintered at 600 °C) were made from powders (∼13 nm) prepared by the gas-condensation technique. Impedance spectra were taken as a function of temperature over the range 450–600 °C and as a function of oxygen partial pressure over the range 10−3−1 atm (550 and 600 °C only). The activation energy was determined to be 55 kJ/mole (0.57 eV) and was independent of oxygen partial pressure. The oxygen partial pressure exponent was −1/6. Impedance spectra exhibited nonlinear I-V behavior, with a threshold of approximately 6 V. These results indicate that grain boundaries are governing the electrical properties of the compact. Ramifications for oxygen sensing and for grain boundary defect characterization are discussed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.