We investigate the optical properties of two sets of Si-doped GaN epitaxial layers with different degree of compensation. The electron concentration dependence of the band-gap energy measured by photoluminescence is interpreted as band-gap narrowing effect and evaluated by a simple relation. The photoluminescence peak positions of heavily compensated samples are shifted downward with respect to those of moderately compensated samples, and the down shift becomes larger at higher electron density. Based on analysis of photoluminescence spectra, these prominent behaviors are accounted for by band-edge potential fluctuation associated with inhomogeneous residual impurities.
The influences of the laser lift-off (LLO) process on the InGaN/GaN blue light emitting diode (LED) structures, grown on sapphire substrates by low-pressure metalorganic chemical vapor deposition, have been comprehensively investigated. The vertical LED structures on Cu carriers are fabricated using electroplating, LLO, and inductively coupled plasma etching processes sequentially. A detailed study is performed on the variation of defect concentration and optical properties, before and after the LLO process, employing high-resolution transmission electron microscopy (HRTEM), scanning electron microscopy (SEM) observations, cathodoluminescence (CL), photoluminescence (PL), and high-resolution X-ray diffraction (HRXRD) measurements. The SEM observations on the distribution of dislocations after the LLO show well that even the GaN layer near to the multiple quantum wells (MQWs) is damaged. The CL measurements reveal that the peak energy of the InGaN/GaN MQW emission exhibits a blue-shift after the LLO process in addition to a reduced intensity. These behaviors are attributed to a diffusion of indium through the defects created by the LLO and creation of non-radiative recombination centers. The observed phenomena thus suggest that the MQWs, the active region of the InGaN/GaN light emitting diodes, may be damaged by the LLO process when thickness of the GaN layer below the MQW is made to be 5 μm, a conventional thickness. The CL images on the boundary between the KrF irradiated and non-irradiated regions suggest that the propagation of the KrF laser beam and an accompanied recombination enhanced defect reaction, rather than the propagation of a thermal shock wave, are the main origin of the damage effects of the LLO process on the InGaN/GaN MQWs and the n-GaN layer as well
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.