Cenospheres (microspheres) are silica-alumina fly ash lightweight fractions obtained from burning pulverized coal. These fractions are characterized by spherical particle shapes of 40 to 400 μm diameter (apparent bulk density 400 kg/m3). The thermal-insulation properties of microspheres are useful. A binder that ensures good strength and improves thermalinsulation properties of bonded materials is hydrated sodium silicate. These microsphere materials are characterized by: (a) apparent bulk density in the compressed state from 400 to 500 kg/m3, (b) compressive strength up to 6 MPa, (c) average mean heat capacity of 500 kJ/m3K at temperatures from 298 to 993 K, and (d) thermal conductivity in the range 0.13 to 0.38 W/mK at temperatures from 298 to 1273 K. The investigation made it possible to optimize the material composition for particular applications. Microsphere materials with silicate binders can be used in the building industry, in heating equipment, and in metallurgical and foundry work.
STRESZCZENIEWiększość produktów odsiarczania spalin charakteryzuje znacząca rozpuszczalność w wodzie i pylenie w stanie suchym. Właściwości te mogą być powodem dużego zanieczyszczenia powietrza, wód i gleb. Spośród wielu sposobów utylizacji tych odpadów, bardzo skuteczny jest proces aglomeracji metodą granulowania lub brykietowania. Z produktów odsiarczania można uzyskać nowy materiał o właściwościach kruszyw budowlanych, przy czym materiał ten jest odporny na erozją wodną i wietrzną, a także na warunki transportu i składowania. W pracy przedstawiono wyniki przeprowadzonych przemysłowych prób granulowania i brykietowania wapniowych produktów odsiarczania spalin. Do granulowania wykorzystano mieszankę fosfogipsu z popiołem lotnym (w udziale 1:5). Otrzymany granulat charakteryzował się wytrzymałością na ściskanie wynoszącą 41,6 MPa, wytrzymałością zrzutową 70% oraz ścieralnością 14,2%. Granulat ten zastosowano do produkcji mieszanki cementowej. Wyprodukowana zaprawa betonowa miała dłuższy czas wiązania i twardnienia w porównaniu do tradycyjnej zaprawy popiołowo-gipsowej, oraz miała większą lub porównywalną wytrzymałość na zginanie i ściskanie podczas twardnienia. Próby brykietowania wykonano z produktu zwanego gipsem syntetycznym lub rea-gipsem zarówno w czystej postaci, jak i z dodatkiem 5% oraz 10% pyłów wapiennych. Brykiety miały dużą wytrzymałość początkową oraz odporność na ścieranie. Wartości tych parametrów zwiększyły się po 72 godzinach sezonowania. Stwierdzono większą odporność brykietów z rea-gipsów na oddziaływanie zmiennych warunków atmosferycznych oraz większą odporność na wymywalność składników rozpuszczalnych w wodzie w porównaniu do brykietów z popiołów lotnych.Słowa kluczowe: produkty odsiarczania spalin, granulowanie, brykietowanie, fosfogips, gips. GRANULATION AND BRIQUETTING OF SOLID PRODUCTS FROM FLUE GAS DESULFURIZATIONABSTRACT Most flue gas desulfurization products can be characterized by significant solubility in water and dusting in dry state. These characteristics can cause a considerable pollution of air, water, and soil. Among many approaches to utilization of this waste, the process of agglomeration using granulation or briquetting has proved very effective. Using desulfurization products a new material of aggregate characteristics has been acquired, and this material is resistant to water and wind erosion as well as to the conditions of transportation and storage. The paper presents the results of industrial trials granulation and briquetting of calcium desulphurization products. The granulation of a mixture of phosphogypsum used with fly ash (in the share 1:5). The resulting granules characterized by a compressive strength of 41.6 MPa, the damping resistance of 70% and 14.2% abrasion. The granulate was used for the production of cement mix. The produced concrete mortar have a longer setting and hardening time, as compared to the traditional ash and gypsum mortar, and have a higher or comparable flexural and compressive strength during hardening. Briquetting trials made of a product c...
WPROWADZENIEMimo, że już wiele lat temu opracowano i wdrożono techniki zabezpieczania materiałów sypkich przed pyleniem, to nadal notuje się przypadki dużego zapylenia terenów wokół składowisk odpadów drobnoziarnistych, zwłaszcza paleniskowych (rys. 1) [Maliszewski 2014, Rogowska 2016.W naszym kraju zabezpieczenie przed pyleniem dokonano po raz pierwszy w 1972 roku na wyłączonym z eksploatacji składowisku w Elektrowni Łaziska, z inicjatywy ówczesnego wojewody, gen. J. Ziętka [Hycnar, Szczygielski 2013]. Kolejne zabezpieczenie składowiska przed pyleniem zrealizowano w Elektrowni Jaworzno II. W następnych latach sukcesywnie wprowadzano zabezpieczanie składowisk, z rekordem rocznym wynoszącym 320 ha składowisk odpadów ze spalania węgla kamiennego przy wykorzystaniu dwóch śmigłowców. Inżynieria Ekologiczna METHODS OF DUST PREVENTION FROM LANDFILLS OF RAW MATERIALS AND WASTE ABSTRACTThe article presents an overview of the solutions to the problem consisting in dusting of raw materials and finegrained waste collected on landfills. The specific physicochemical properties of loose materials and unfavorable atmospheric conditions are responsible for the heavy pollution of the environment by dust, posing a threat to human health. The types of materials that are potential sources of dust pollution are presented. The methods of eliminating and limiting dustiness of loose powders, often used in industry, engineering, communal and emergency situations, are discussed. Examples of domestic and foreign solutions to prevent dusting and to protect the waste deposit from erosion are shown. In conclusion, the existing safety techniques have been found to be effective in preventing raw materials and waste from dusting.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.