We demonstrate a rapid, accurate, and convenient method for tailoring the optical properties of diamond surfaces by employing laser induced periodic surface structuring (LIPSSs). The characteristics of the fabricated photonic surfaces were adjusted by tuning the laser wavelength, number of impinging pulses, angle of incidence and polarization state. Using Finite Difference Time Domain (FDTD) modeling, the optical transmissivity and bandwidth was calculated for each fabricated LIPSSs morphology. The highest transmission of ~99.5% was obtained in the near-IR for LIPSSs structures with aspect ratios of the order of ~0.65. The present technique enabled us to identify the main laser parameters involved in the machining process, and to control it with a high degree of accuracy in terms of structure periodicity, morphology and aspect ratio. We also demonstrate and study the conditions for fabricating spatially coherent nanostructures over large areas maintaining a high degree of nanostructure repeatability and optical performance. While our experimental demonstrations have been mainly focused on diamond anti-reflection coatings and gratings, the technique can be easily extended to other materials and applications, such as integrated photonic devices, high power diamond optics, or the construction of photonic surfaces with tailored characteristics in general.
Figure 1. (a) AFM analysis of the LIPSSs height and aspect ratio A as function of fluence and scanning speed. (b) Average and standard deviation of structure profiles from fabricated nanopatterns with different A generated with: 3.12 J/cm 2 and 200 μm/s (high A), 2.8 J/cm 2 and 150 μm/s (intermediate A), 2.19 J/cm 2 and 200 μm/s (low A).
A diffractive optical element was fabricated by monolithically integrating two volume phase-gratings (VPGs) in the bulk of a single-piece transparent material. A computer model of the diffraction generated by the double volume phase-grating (DVPG) was made with a rigorous coupled wave analysis simulator. Simulations and experiments show that the diffractive behavior of a DVPG can be controlled by arranging the relative displacement and the distance between the VPGs according to Talbot self-imaging planes. In order to diffract the total incident light, the phase accumulation in the VPGs has to be π/2, which was achieved by single-scan femtosecond laser processing of a nanocrystal doped glass as the substrate material. Ex situ microscope images of the cross-sections are presented for laser processed lines in the form of VPGs and DVPGs. The far-field diffraction of DVPGs formed by selectively located VPGs was characterized with a monochromatic 633 nm and a supercontinuum white light. Functional designs of high diffraction efficiency with potential applications in photonics were successfully fabricated in a one-step and free of chemicals process.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.